Zhang, Bin; Guo, Wei; Yu, Yi; Zhai, Chengcheng; Qi, Sisheng; Yang, Anping; Li, Lei; Yang, Zhiyong; Wang, Rongping; Tang, Dingyuan; Tao, Guangming; Luther-Davies, Barry
Journal of the American Ceramic Society, 20/May , Letnik: 98, Številka: 5Journal Article
High‐purity Ge–As–Se and Ge–As–S chalcogenide glasses were prepared by modified physical and chemical purification techniques. Using the purified glasses, step‐index fibers with a small core (~5.5 μm) and large numerical aperture (~1.3) were fabricated. When a 13.5‐cm‐long fiber was pumped with 320 fs pulses at a repetition rate of 10.5 MHz at 4.1 μm, supercontinuum spanning from ~1.8 to ~9.8 μm with a dynamic range of ±10 dB and an average power of ~3 mW was generated.
Avtor
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.