Nakamura, H.; Takanashi, M.; Itoh, T.; Wu, M.; Shimizu, Y.
International journal of fatigue, 07/2011, Letnik: 33, Številka: 7Journal Article
This paper deals with multiaxial low cycle fatigue crack behavior of Ti–6Al–4V under non-proportional loading. Strain controlled fatigue tests under proportional loading and non-proportional loading with 90° out-of-phase difference between the axial and shear strains ε and γ were carried out on tubular specimens at room temperature. As a result, Mises strain based fatigue lives under non-proportional loading were approximately 1/10 of those under proportional loading. The specimen surfaces were observed to evaluate life reduction. These results showed that non-proportional loading caused 10 times more cracks than those of proportional loading. Non-proportional loading changes directions of the principal stress and strain axes, and high shear stresses acting on many planes stimulate more slip planes. Consequently, non-proportional loading resulted in many cracks. In addition, the high shear stresses also resulted in larger misorientation under non-proportional loading. The crack initiation life defined as the length 2 a of 30 μm did not differ significantly between proportional loading and non-proportional loading. However, the fatigue cracks under non-proportional loading propagated faster those under proportional loading. This is because the fatigue cracks under non-proportional loading are subjected to more severe strain field than those under proportional loading, even though the crack size and applied strain are the same. Thus, the significant reduction in fatigue life under non-proportional loading is caused by the accelerated crack growth due to a higher strain intensity factor.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.