Liu, Dashuang; Wei, Ping; Long, Weimin; Zhou, Wei; Wu, Mingfang; Wang, Jiayou
Science and technology of welding and joining, 20/1/2/, Letnik: 26, Številka: 1Journal Article
The effect of ER5356 and ER5087 welding wires on fatigue property of MIG-welded 7N01-T4 aluminium alloy joints was investigated. The microstructure of ER5087 welded joint is similar to that of ER5356 joint. However, the fusion zone of the welding joint with ER5087 has a smaller grain size than that of the joint with ER5356. The fatigue strength of joints welded with ER5356 and ER5087 is 105.9 and 103.2 MPa at 10 7 cycles. During the fatigue process, the crack initiation for joints welded using ER5087 is due to porosity while for ER5356 is due to microcracks from eutectic melting in the heat-affected zone.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.