Liu, Hu-Lin; Liu, Ji-Xuan; Liu, Hai-Tao; Zhang, Guo-Jun
Ceramics international, 07/2015, Letnik: 41, Številka: 6Journal Article
Oxidation behavior of ZrB2–SiC ceramics containing 0, 10 and 20vol% ZrC was studied at 1600°C in stagnant air. The structures of oxide scales depended on ZrC content. The thickness of the SiO2-rich glass layer on the outermost surface decreased steeply with the addition of ZrC. One “ZrC-corroded layer”, containing ZrCxOy, SiC and ZrB2, was observed in ZrB2–SiC–ZrC. The oxidation kinetics was converted from parabolic to linear for the ceramics with 20vol% ZrC.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.