Cui, Wei; King, Daniel R.; Huang, Yiwan; Chen, Liang; Sun, Tao Lin; Guo, Yunzhou; Saruwatari, Yoshiyuki; Hui, Chung‐Yuen; Kurokawa, Takayuki; Gong, Jian Ping
Advanced materials (Weinheim), 08/2020, Letnik: 32, Številka: 31Journal Article
Soft fiber‐reinforced polymers (FRPs), consisting of rubbery matrices and rigid fabrics, are widely utilized in industry because they possess high specific strength in tension while allowing flexural deformation under bending or twisting. Nevertheless, existing soft FRPs are relatively weak against crack propagation due to interfacial delamination, which substantially increases their risk of failure during use. In this work, a class of soft FRPs that possess high specific strength while simultaneously showing extraordinary crack resistance are developed. The strategy is to synthesize tough viscoelastic matrices from acrylate monomers in the presence of woven fabrics, which generates soft composites with a strong interface and interlocking structure. Such composites exhibit fracture energy, Γ, of up to 2500 kJ m−2, exceeding the toughest existing materials. Experimental elucidation shows that the fracture energy obeys a simple relation, Γ = W · lT, where W is the volume‐weighted average of work of extension at fracture of the two components and lT is the force transfer length that scales with the square root of fiber/matrix modulus ratio. Superior Γ is achieved through a combination of extraordinarily large lT (10–100 mm), resulting from the extremely high fiber/matrix modulus ratios (104–105), and the maximized energy dissipation density, W. The elucidated quantitative relationship provides guidance toward the design of extremely tough soft composites. Novel soft fiber‐reinforced polymers (FRPs) are developed by using viscoelastic polymers that are adhesive, soft, and tough as matrices. The unique combination of these properties in the matrices ensures a strong component interface, which consequently maximizes the energy dissipation density and gives rise to a large force transfer length enabled by the extremely high fiber/matrix modulus ratio. As a result, the soft FRPs can achieve toughness of up to 2500 kJ m−2, exceeding any existing best‐in‐class materials.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.