Synthesis of Tin Dioxide Octahedral Nanoparticles with Exposed High-Energy {221} Facets and Enhanced Gas-Sensing Properties

E-viri

Recenzirano

Synthesis of Tin Dioxide Octahedral Nanoparticles with Exposed High-Energy {221} Facets and Enhanced Gas-Sensing Properties

Han, Xiguang; Jin, Mingshang; Xie, Shuifen; Kuang, Qin; Jiang, Zhiyuan; Jiang, Yaqi; Xie, Zhaoxiong; Zheng, Lansun

Angewandte Chemie (International ed.), November 16, 2009, Letnik: 48, Številka: 48

Journal Article

Selective exposure of high‐energy {221} facets with many surface dangling bonds, (111) terraces, and (110) steps (bottom picture) at the surface of octahedral SnO2 nanoparticles (top) through a simple hydrothermal synthesis route gives them enhanced gas‐sensing performance over particles with other shapes, whereby the sensing activity is proportional to the fraction of {221} facets among the exposed surfaces.

Išči dalje

Avtor

Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.

Leto	Faktor vpliva		Izdaja		Kategorija		Razvrstitev
Leto	JCR	SNIP	JCR	SNIP	JCR	SNIP	JCR	SNIP

Povezave do osebnih bibliografij avtorjev	Povezave do podatkov o raziskovalcih v sistemu SICRIS

Vir: Osebne bibliografije in: SICRIS

Naloži sliko

Vnos na polico

Dodajanje gradiva na polico je uspelo.

Dodajanje gradiva na polico je spodletelo.

Dodajanje gradiva na polico ni bilo potrebno.

Trajna povezava

E-pošta

Faktor vpliva

Izberite knjižnično izkaznico:

Baze podatkov, v katerih je revija indeksirana

Citiranje

Tema