Bi, Wenhui; Guo, Qingbin; Zhang, Tengfei; He, Yan; Liu, Qing
International journal of hydrogen energy, 06/2024, Letnik: 71Journal Article
To elucidate the effect of solution viscosity on the synthesis of Ni-phyllosilicate, polyacrylamide was incorporated to create a viscous aqueous medium containing of sodium metasilicate, nickel nitrate and NH4F. The enhanced viscosity promotes the dispersion of the initial formed crystal seeds and the growth of Ni-phyllosilicate, culminating in a Ni-rich NiPs-RT-6 of a high Ni content of up to 55.2 wt%. Residual polyacrylamide elimination was accomplished via calcination, concurrently enhancing metal-support interaction. The as-synthesized samples display a nanoflower morphology with nanospheres overlaid with numerous thin nanosheets. The relatively small Ni particles around 5.7 nm were obtained after reduction even at a very high Ni loading, owing to its strong metal-support interaction. NiPs-RT-6 achieves a CO2 conversion of 75.9% at 450 °C, 0.1 MPa, 60 L g−1·h−1, which closely approximates thermodynamic equilibrium. The turn over frequency for CO2 (TOFCO2) was substantial, calculated at 3.7 × 10−3 s−1, accompanied by activation energy (Ea) of 80.6 kJ·mol–1. In-situ Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) further disclosed that m-HCOO– serves as a crucial intermediate following a formate reaction pathway. With its high Ni content, finely distributed Ni particles, and strong metal-support interaction, NiPs-RT-6 demonstrates promising catalytic activity in CO2 methanation. Display omitted •The room-temperature synthesis of Ni-phyllosilicate was achieved.•A viscous solvent of polyacrylamide significantly promoted the synthesis of Ni-phyllosilicate.•The reduced Ni-phyllosilicate retained small Ni particles at a high Ni content.•Polyacrylamide improved the catalytic performance of CO2 methanation.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.