Somekawa, Hidetoshi; Tsuru, Tomohito
Scripta materialia, 03/2017, Letnik: 130Journal Article
The impact of alloying elements on crack propagation and atomistic phenomenon at {101¯2}-type twin boundaries in magnesium was investigated via both experiments and calculations. The alloying elements clearly affected the crack propagation behavior. Cracks were difficult to propagate along matrix-deformation twinning interfaces in alloys that had high fracture toughness. In such magnesium alloys, the solute atoms, e.g., silver, manganese and zinc atoms, create adhesive interactions between magnesium atoms. Closed-shell and covalent-like bonding of these types of solute atoms would influence strong adhesion, which impedes the nucleation of a new surface at the twin boundary. Display omitted
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.