GORZKOWSKI, E. P; PAN, M.-J; BENDER, B; WU, C. C. M
Journal of electroceramics, 08/2007, Letnik: 18, Številka: 3-4Journal Article
Barium strontium titanate glass-ceramics were successfully produced with one major crystalline phase when Al^sub 2^O^sub 3^ was added to the melt. A dielectric constant of 1000 and a breakdown strength of 800 kV/cm was achieved; however the energy density was only measured to be 0.3-0.9 J/cm^sup 3^. These energy density values were lower than anticipated due to the presence of dendrites and pores in the microstructure. Using BaF^sub 2^ as a refining agent improved the microstructure and doubled the energy density for BST 80/20 samples. However, no refining agent reduced the increasing amount of hysteresis that developed with increasing applied electric field. This phenomenon is believed to be due to interfacial polarization.PUBLICATION ABSTRACT
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.