Xu, Zhuang Zhuang; Gao, Li Qiang; Yin, Qian; Lian, Ye Da; Wen, Zhi Xun
Materials science forum, 2021, Letnik: 1018Journal Article
Effects of different loading and uninstalling and safe loading time on the low-cycle fatigue-creep interaction behavior of GH4169 superalloy at 650°C/850MPa have been investigated. The study found that under the safe loading time, with the longer the loading and unistalling time, the fatigue-creep property and life of this alloy were gradually improved. However, under the same loading and uninstalling time, with the extension of the loading time, property of the fatigue-Creep of the alloy was gradually reduced, and its life was gradually shortened. In addition, The fracture failure behavior of the alloy under different conditions was studied in detail. Interestingly, With the extension of the holding time, the fracture failure of the alloy was changed from fatigue damage to creep damage, which makes its fracture mode transition the transgranular fracture into intergranular fracture extension.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.