Liao, Ning; Jia, Dechang; Yang, Zhihua; Zhou, Yu
Journal of advanced ceramics, 03/2019, Letnik: 8, Številka: 1Journal Article
Bulk Si 2 BC 3 N ceramics were reinforced with SiC coated multi-walled carbon nanotubes (MWCNTs). The phase compositions, mechanical properties, and thermal shock resistance, as well as the oxidation resistance of the designed Si 2 BC 3 N ceramics were comparatively investigated. The results show that nano SiC coating can be formed on MWCNTs through pyrolyzing polysilazane, which improves the oxidation resistance of MWCNTs. A stronger chemical bonding is formed between the SiC coated MWCNTs and SiC particles, contributing to improved flexural strength (532.1 MPa) and fracture toughness (6.66 MPa·m 1/2 ). Besides, the 2 vol% SiC coated MWCNTs reinforced Si 2 BC 3 N ceramics maintains much higher residual strength (193.0 MPa) after thermal shock test at 1000 °C. The enhanced properties should be attributed to: (1) the breaking of MWCNTs and the debonding between MWCNTs and SiC interfaces, which leads to more energy dissipation; (2) the rough surfaces of SiC coated MWCNTs increase the adhesion strength during the “pull out” of MWCNTs.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.