Wang, Yinchen; Li, Peng; Zhang, Liangliang; Ding, Zhijie; Li, Chao; Li, Jiachen; Jiang, Xin; Dong, Honggang
Materials & design, August 2024, 2024-08-00, 2024-08-01, Letnik: 244Journal Article
Display omitted •A high entropy interlayer (TiZrHfNb)95Al5 was successfully designed for diffusion bonding of GH4169 to Ti2AlNb.•The relationships between grain characteristics, lattice mismatch and mechanical properties, fracture mechanisms were revealed.•The major cracks located at the elastic modulus dramatically changed interface, i.e., the no-coherent interface.•The highest shear strength reached 384 MPa at 980 °C for 90 min. A high entropy interlayer (TiZrHfNb)95Al5 was successfully designed for vacuum diffusion bonding of GH4169 superalloy to Ti2AlNb alloy. The relationships between grain size, grain boundary, lattice mismatch and microhardness, elastic modulus, shear strength and fracture behaviors were revealed. The typical microstructure was Ti2AlNb/B2/Solid solution/(Ti, Zr, Hf)2(Ni, Nb)+(Ti, Zr, Hf)(Ni, Nb) + Solid solution/(Ti, Zr, Hf)(Ni, Nb) + (Cr, Ni, Fe)ss/(Cr, Ni, Fe)ss/Cr-rich(Cr, Ni, Fe)ss/Ni-rich(Cr, Ni, Fe)ss/GH4169. With the holding time increased, the shear strength overall increased and decreased sharply, and the highest shear strength reached 384 MPa at 980 °C for 90 min. The microstructure had anisotropic crystal orientation, and the joints of Zone Ш for 90 min consisted of 92.08 % HAGBs and 7.92 % LAGBs. The residual strains and stresses decreased when the holding time increased. Meanwhile, recrystallisation appeared in Zone Ш, and the increase in the recrystallisation rate led to grain refinement. The lattice mismatch between (Ti, Zr, Hf)(Ni, Nb) and (Cr, Ni, Fe)ss phases was 25.05 %, indicating that the interface was non-coherent, and (Ti, Zr, Hf)(Ni, Nb)+(Cr, Ni, Fe)ss phases were located at an elastic modulus dramatically changed interface. Thus, the cracks easily formed in this interface and led to joint fracture. Moreover, the fracture mechanism was brittle fracture.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.