Thermomagnetic analysis of amorphous (Co xFe 1 −x) 73.5Nb 3Cu 1Si 13.5B 9 metallic glasses

E-viri

Recenzirano

Thermomagnetic analysis of amorphous (Co xFe 1 −x) 73.5Nb 3Cu 1Si 13.5B 9 metallic glasses

Fernández, A.; Pérez, M.J.; Tejedor, M.; Madurga, V.

Journal of magnetism and magnetic materials, 2000, Letnik: 221, Številka: 3

Journal Article

Metallic glass samples of (Co x Fe 1− x ) 73.5Nb 3Cu 1Si 13.5B 9 are studied by thermomagnetic analysis. The Curie temperature increases with the substitution of Fe by Co, and crystallization temperature decreases. A simple consideration of the alloy as the sum of two magnetic systems is applied with good results. The observed discrepancies are explained as due to a magnetic interaction between the Co and Fe atoms.

Išči dalje

Avtor

Fernández, A. | Pérez, M.J. | Tejedor, M. | Madurga, V.

Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.

Leto	Faktor vpliva		Izdaja		Kategorija		Razvrstitev
Leto	JCR	SNIP	JCR	SNIP	JCR	SNIP	JCR	SNIP

Povezave do osebnih bibliografij avtorjev	Povezave do podatkov o raziskovalcih v sistemu SICRIS

Vir: Osebne bibliografije in: SICRIS

Naloži sliko

Vnos na polico

Dodajanje gradiva na polico je uspelo.

Dodajanje gradiva na polico je spodletelo.

Dodajanje gradiva na polico ni bilo potrebno.

Trajna povezava

E-pošta

Faktor vpliva

Izberite knjižnično izkaznico:

Baze podatkov, v katerih je revija indeksirana

Citiranje

Tema