Determination of shear bond strength between PEEK composites and veneering composites for the production of dental restorations [Elektronski vir]Kuchler, Anamarija ...We studied the shear bond strength (SBS) of two PEEK composites (BioHPP, BioHPP plus) with three veneering composites: Visio.lign, SR Nexco and VITA VM LC, depending on the surface treatment: ... untreated, sandblasted with 110 μm Al2O3, sandblasted and cleaned ultrasonically in 80% ethanol, with or without adhesive Visio.link, with applied Visio.link and MKZ primer. For the BioHPP plus, differential scanning calorimetry (DSC) revealed a slightly lower glass transition temperature (Tg 150.4 ± 0.4 °C) and higher melting temperature (Tm 339.4 ± 0.6 °C) than those of BioHPP (Tg 151.3 ± 1.3 °C, Tm 338.7 ± 0.2 °C). The dynamical mechanical analysis (DMA) revealed a slightly higher storage modulus of BioHPP (E’ 4.258 ± 0.093 GPa) than of BioHPP plus (E′ 4.193 ± 0.09 GPa). The roughness was the highest for the untreated BioHPP plus, and the lowest for the polished BioHPP. The highest hydrophobicity was achieved on the sandblasted BioHPP plus, whereas the highest hydrophilicity was found on the untreated BioHPP. The highest SBSs were determined for BioHPP and Visio.lign, adhesive Visio.link (26.31 ± 4.17 MPa) or MKZ primer (25.59 ± 3.17 MPa), with VITA VM LC, MKZ primer and Visio.link (25.51 ± 1.94 MPa), and ultrasonically cleaned, with Visio.link (26.28 ± 2.94 MPa). For BioHPP plus, the highest SBS was determined for a sandblasted surface, cleaned ultrasonically, with the SR Nexco and Visio.link (23.39 ± 2.80 MPa).Source: Materials [Elektronski vir]. - ISSN 1996-1944 (Vol. 16, iss. 9, [article no.] 3286, April 2023, 18 str.)Type of material - e-article ; adult, seriousPublish date - 2023Language - englishCOBISS.SI-ID - 150518531
Author
Kuchler, Anamarija |
Pušnik Črešnar, Klementina |
Švab, Iztok |
Vuherer, Tomaž |
Žigon, Majda |
Brunčko, Mihael
Topics
CAD/CAM rezkanje |
stiskanje |
toplotni prehodi PEEK kompozitov |
hrapavost |
omočljivost |
trdnost strižne vezi |
BioHPP |
CAD/CAM milling |
BioHPP plus |
pressing |
veneering composites |
roughness |
wettability |
shear bond strength
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Author | Kuchler, Anamarija ... |
Title | Determination of shear bond strength between PEEK composites and veneering composites for the production of dental restorations [Elektronski vir] |
Publication date | 2023-04-22 |
COBISS.SI-ID | 150518531 |
Publication version in repository | Publisher's version |
Publication licence | Creative Commons Attribution 4.0 International |
Embargo | Immediate publication for public |
Project(s) from which the publication was funded
Title | Acronym | Project ID | Funder |
---|---|---|---|
Tehnologije metastabilnih materialov | P2-0120-2022 |
Javna agencija za znanstvenoraziskovalno in inovacijsko dejavnost Republike Slovenije |
|
Tekstilna kemija in napredni tekstilni materiali | P2-0118-2022 |
Javna agencija za znanstvenoraziskovalno in inovacijsko dejavnost Republike Slovenije |
Files that belong to the publication
Link |
---|
![]() |
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|---|
Kuchler, Anamarija | ![]() |
Pušnik Črešnar, Klementina | 34450 |
Švab, Iztok | 22426 |
Vuherer, Tomaž | 15682 |
Žigon, Majda | 06126 |
Brunčko, Mihael | 20229 |
Select pickup location:
Material pickup by post
Notification
Subject headings in COBISS General List of Subject Headings
Select pickup location
Pickup location | Material status | Reservation |
---|
Please wait a moment.