Ma, Xue; Wang, Zhijun; Tong, Xuezhu; Du, Xaoming; Li, Tianfu; Liu, Rongdeng; Liu, Yuntao; Chen, Dongfeng
Materiali in tehnologije, 04/2022, Volume: 56, Issue: 2Journal Article
Microstructure evolution and mechanical properties in an Fe-17Cr-4Ni-4Cu alloy aged at 475 °C after different aging times were studied. Conventional transmission electron microscopy (TEM) and high-resolution electron microscopy (HREM) studies revealed the formation of 9R-structure Cu-rich precipitates and Cr-rich α’ phase by spinodal decomposition in the samples aged at 475 °C after 100–1000 h. The fine Cu-rich precipitates and Cr-rich α’ phase by spinodal decomposition lead to a significant increase in the hardness, together in the early stages (100 h). Continued aging to 500 h leads to increased precipitation of the Cr-rich α’, which provides significant strengthening, reaching maximum hardening, despite the continued loss of hardening by weakening by the Ostwald ripening of the Cu-rich precipitates. Extending the aging time to 1000 h leads to substantial reversed austenite transformation and a large number of ripening -copper precipitates that causes softening. The results of the impact tests showed that the major fracture mode was cleavage and/or quasi-cleavage.
Author
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.