Zhang, Jintao; Wang, Shibo; Ding, Hua; Hu, Peng; Huang, Yi; Zhang, Yu
Crystals, 08/2023, Volume: 13, Issue: 8Journal Article
High-pressure torsion (HPT) was applied for the Ni49.6Ti35.4Hf15 (at.%) alloy up to 1/4, 2 and 16 turns under a pressure of 4.0 GPa. The samples were examined using X-ray diffraction (XRD), transmission electron microscope (TEM) and microhardness measurements. The results indicate that the mixture of an amorphous and nanocrystalline microstructure developed in the investigated NiTiHf alloy as the number of HPT turns was increased to two. The average hardness of the samples increased from 330 Hv to 500 Hv after 16 turns of HPT. Very fine martensite developed when the HPT-processed samples were annealed at 550 °C and the finer microstructures were attained with higher HPT turns. Differential scanning calorimetry (DSC) tests were performed in the post-HPT annealing samples to clarify the transformation behavior after severe plastic deformation in HPT and subsequent annealing, so as to provide an experimental basis for the application of the shape memory alloy. The transformation temperature of the alloy decreased remarkably when the number of turns of HPT reached 16. It is suggested that the deformation extent and annealing temperatures should be considered in order to maintain a high transformation temperature while utilizing the strengthening effect of HPT in the NiTiHf alloy.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.