Xu, Q; Guan, H Q; Zhong, Z H; Huang, S S; Zhao, J J
Scientific reports, 01/2021, Volume: 11, Issue: 1Journal Article
When face-centered cubic (FCC) metals and alloys with low stacking fault energy (SFE) are irradiated by high-energy particles or deformed at high speed, stacking fault tetrahedra (SFTs), which are a type of vacancy cluster defect, are often formed. Therefore, SFTs were expected to form in the CoCrFeMnNi equiatomic high-entropy alloy (HEA). However, no SFT was observed in the CoCrFeMnNi HEA with high-speed plastic deformation even after annealing at 873 K. To elucidate this mechanism, the binding energy of vacancy clusters in the CoCrFeMnNi HEA was calculated based on first principles. The binding energy of the di-vacancy cluster was positive (average of 0.25 eV), while that of the tri-vacancy cluster was negative (average of - 0.44 eV), suggesting that the possibility of formation of a tri-vacancy cluster was low. The inability to form a cluster containing three vacancies is attributed to the excellent irradiation resistance of the CoCrFeMnNi HEA. However, if an extra vacancy is added to a tri-vacancy cluster (with negative binding energy), the binding energy of the subsequent tetra-vacancy cluster may become positive. This suggests that it is possible to form vacancy clusters in the CoCrFeMnNi HEA when high-energy ion or neutron irradiation causes cascade damage.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.