Shao, Mingqiang; Li, Ying; Shi, Yiran; Liu, Jiangtao; Xue, Baoxia; Niu, Mei
Polymers, 04/2023, Volume: 15, Issue: 9Journal Article
It is difficult to enhance the char yields of polypropylene (PP) due to the preferential complete combustion. Successful formation of abundant char layer structure of PP upon flammability was obtained due to the synergistic effect of NiO, Alsub.2Osub.3 and activated carbon (AC). From characterization of scanning electron microscopy (SEM) and transmission electron microscopy (TEM), it was revealed that the microstructure of residual char contained large amount of carbon nanotubes. Compared to the modification of AC, NiO and Alsub.2Osub.3 alone, the combination of AC, NiO and Alsub.2Osub.3 dramatically promotes the charring ability of PP. In the case of AC and NiO, NiO plays a role of dehydrogenation, resulting in the degradation product, while AC mainly acts as carbonization promoter. The addition of Alsub.2Osub.3 results in higher dispersion and smaller particle size of NiO, leading to greater exposure of active sites of NiO and higher dehydrogenation and carbonization activity. Compared to the neat PP, the decomposition temperature of the PP modified by combined AC, NiO and Alsub.2Osub.3 was increased by 90 ℃. The yield of residual char of AC-5Ni-Al-PP reached as high as 44.6%. From the cone calorimeter test, the heat release rate per unit area (HRR) and total heat release per unit area (THR) of PP composite follows the order AC-5Ni-Al-PP < AC-10Ni-Al-PP < AC-Ni-PP < AC-15Ni-Al-PP < AC-1Ni-Al-PP. Compared to the neat PP, the peak of HRR declined by 73.8%, 72.7%, 71.3%, 67.6% and 62.5%, respectively.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.