Internal oxidation of rapidly solidified ternary copper alloys. Part II, An experimental studyAnžel, Ivan, inženir metalurgije in materialov ; Kneissl, Albert C. ; Kosec, LadislavA new model of the effective particles formation in the copper alloys, presented in Part I, was studied experimeentally by the internal Oxidation of rapidly solidified ternary Cu-Al-Zr alloys and was ... confirmed with the results that are shown in this paper. With the rapid solidification process the size of the intermetallic Cu-Zr regions in the copper matrix was reduced to a scale which enabled dissolution of the intermetallic particless ahead of the advancing front of the internal oxidation process. An appropriately chosenconcentration of the soluble alloying element (C Al>1 at.%) and the diffusion of Zr down the concentration gradient to the internal oxidation front made possible the heterogeneous precipitation of zirconium oxide (ZrO2) from the solid solution and its growth on alumina particless (Al2O3) formed before. Because of higher dimensional stability of ZrO2 and crystal structure that provides a larger lattice mistif at the interface with the Cu matrix than that of gama-Al2O3 we obtained more effective oxide particles for dispersion strengening at higher temperatures.Vir: Zeitschrift für Metallkunde : international journal of materials research. - ISSN 0044-3093 (Bd. 90, Heft 8, 1999, str. 630-636)Vrsta gradiva - članek, sestavni delLeto - 1999Jezik - angleškiCOBISS.SI-ID - 4719382
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Zeitschrift für Metallkunde : international journal of materials research. - ISSN 0044-3093 (Bd. 90, Heft 8, 1999, str. 630-636)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Anžel, Ivan, inženir metalurgije in materialov | 10369 |
Kosec, Ladislav | 00050 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: