Application of normalization method to fracture toughness testing of welds with pronounced strength heterogeneity : doctoral disertationŠtefane, PrimožThis doctoral dissertation presents the results of an extensive fracture testing programme of welds with pronounced strength heterogeneity. Purpose of this programme was to determine fracture ... toughness of heterogeneous welds that contain a midplane crack. Application of standardized fracture testing methods in heterogeneous welds might lead to overestimation or underestimation of fracture toughness and consequentially to inaccurate assessment of structural integrity. Reasons for that are variations in mechanical properties of different material regions in the weld which have a significant impact on development of deformation at the crack tip, and consequently on the crack driving force. Experimental procedures in scope of this research include fabrication of weld sample plates, that were welded with MAG process. The welds were fabricated using two different electrodes, one with higher and one with lower mechanical properties, with respect to base material S690QL in order to replicate extreme variations of mechanical properties in the weldment. Fabricated welds were then characterized in detail using metallography, three-point bend impact testing, indentation hardness measurements and tensile testing of flat miniature and round bar standard tensile specimens. Resistance of welds to stable tearing was investigated by fracture testing of square surface cracked SE(B) specimens containing a weld midplane notch. J-integral has been estimated from plastic work, using the normalization data reduction method that is included in standard ASTM E1820. The advantage of the normalization data reduction method is that no special equipment or complex testing method is needed to measure ductile crack growth during fracture testing. The ductile crack growth is determined directly from the load-displacement record, by applying appropriate calibration function and physical lengths of initial and final cracks that were measured post-mortem with the nine-point method. Several correction factors had to be calibrated in order to successfully implement the normalization data reduction method to fracture testing of welds with pronounced strength heterogeneity. For that reason, parametric finite element analyses were conducted for several weld configurations. Finite element models incorporated plane strain conditions in order to provide calibrated factors that comply with plane strain equations included in ASTM E1820. Additionally, crack tip constraint has been extensively analysed and correlated with the plastic deformation fields. This clarified altered deformation behaviour of modelled welds in comparison with the base material and corresponding effect on fracture toughness. Finally, calibrated factors were applied to computation of J-integral from data that were measured during fracture testing. J-R resistance curves were constructed for the tested heterogeneous welds and compared to the ones of the base material. This directly showed the effect of variations of mechanical properties on the weld fracture behaviour.Vrsta gradiva - disertacija ; neleposlovje za odrasleZaložništvo in izdelava - Maribor : [P. Štefane], 2022Jezik - angleškiCOBISS.SI-ID - 138416131
Povezava(-e):
Digitalna knjižnica Univerze v Mariboru – DKUM
Digitalna knjižnica Slovenije - dLib.siDostop z namenskih računalnikov v prostorih NUK
Avtor
Štefane, Primož
Drugi avtorji
Gubeljak, Nenad |
Hertelé, Stijn
Teme
Zvarni spoji |
Lom |
Disertacije |
Univerzitetna in visokošolska dela |
weld |
strength mismatch |
fracture |
normalization data reduction technique |
plastic
correction factors |
test fixture |
SE(B) specimen |
J-R resistance curve |
zvar |
trdnostno neujemanje |
lom |
normalizacijska metoda |
plastični
korekcijski faktorji |
vpenjalna priprava |
SE(B) preizkušanec |
J-R odpornostna krivulja |
doktorske disertacije
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Rezervirajte gradivo na želenem mestu prevzema.
Mesto prevzema |
Status gradiva | Rezervacija |
---|---|---|
Časopisna čitalnica |
prosto - za čitalnico
|
|
Velika čitalnica |
prosto - za čitalnico
|
Signatura – lokacija, inventarna št. ... |
Status izvoda |
---|---|
GS II 0000747839 glavno skladišče GS II 747839 glavno skladišče |
prosto - za čitalnico
|
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Štefane, Primož | 37696 |
Gubeljak, Nenad | 10470 |
Hertelé, Stijn | ![]() |
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi