Display omitted
To evaluate the effect of the ceramic processing and aging method on the microstructure, optical, and mechanical properties of a third generation ultra-translucent zirconia, yttria ...partially stabilized zirconia (5Y-PSZ).
In-house discs were obtained through uniaxial and isostatic pressing an ultra-translucent Y-PSZ powder and sintering at 1450 °C for 2 h. As control, a commercial disc was milled from pre-sintered blocks fabricated with the same 5Y-PSZ powder through isostatic pressing and sintered under the same protocol. Discs were allocated into three groups according to aging condition as immediate (non-aged) and aged using autoclave or hydrothermal reactor at 134ºC for 20 h at 2.2 bar. Crystalline content and microstructure were evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Optical properties were determined using reflectance data to calculate the contrast ratio (CR) and translucency parameter (TP). Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength tests.
XRD spectra revealed a prevalence of cubic (70%) and tetragonal (30%) phases, and the SEM images showed a dense fully crystalline ceramic matrix for both materials. Crystalline content and microstructure of the in-house and commercial 5Y-PSZs were not affected by aging. As-sintered 5Y-PSZs demonstrated similar CR (~0.6) and TP (~18) values, as well as Vickers hardness (~14 GPa) and fracture toughness (~3.8 Mpa.m1/2), with no significant alteration after both aging methods. In-house and commercial Y-PSZs Weibull moduli ranged from 3.0 to 5.3. 5Y-PSZ processing methods resulted in similar characteristic strength after sintering (592–618 Mpa). While commercial 5Y-PSZ showed no significant influence of aging on strength, hydrothermal reactor aging significantly decreased the in-house Y-PSZ characteristic strength (474 Mpa). Both 5Y-PSZs demonstrated high reliability up to 300-Mpa strength missions, with no detrimental effect of aging (88–100%).
Irrespective of the processing method, ultra-translucent 5Y-PSZ showed high aging resistance and translucency stability, as well as strength corresponding to the indication up to short-span anterior prostheses.
To characterize the optical and mechanical properties of a commercial and in-house translucent Y-TZP before and after aging in autoclave or hydrothermal reactor.
In-house experimental discs were ...obtained through uniaxial and isostatic pressing a translucent Y-TZP powder and sintering at 1,550 °C/1 h. Commercial discs were milled from pre-sintered blocks fabricated with the same powder through uniaxial and isostatic pressing and sintering. Discs were allocated into three groups according to aging condition: immediate, aged via autoclave, or reactor (134 °C, 20 h, 2.2 bar). Crystalline content and microstructure were evaluated using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Residual compressive stress (CS) was determined by Raman spectroscopy. Optical properties were determined by the contrast ratio (CR) and translucency parameter (TP) using reflectance data. Mechanical properties were assessed by Vickers hardness, fracture toughness and biaxial flexural strength tests.
XRD and SEM revealed a typical Y-TZP crystalline content, chiefly tetragonal phase, and a dense crystalline matrix for both processing protocols. Reactor aging triggered a more pronounced t-m transformation relative to autoclave. In-house and commercial Y-TZPs demonstrated similar CR and TP, with reactor aging significantly increasing their translucency. Similarly, reactor aging influenced Vickers hardness and fracture toughness. In-house processed Y-TZP clearly demonstrated the presence of CS, whereas commercial Y-TZP showed no presence of CS. Non-aged in-house Y-TZP resulted in significantly lower characteristic strength relative to commercial Y-TZP. While aging protocols significantly increased the characteristic strength of in-house Y-TZP, reactor significantly decreased commercial Y-TZP characteristic strength. Both Y-TZP processing protocols demonstrated high reliability at high-stress missions, with no detrimental effect of aging.
Laboratory aging methodology significantly influenced optical and mechanical properties of a commercial and in-house translucent Y-TZP.