This study examined the effects of wood pulp fiber length (short, medium, and long), and fiber loading (27%,
37%, 47%, and 0% non-reinforced PP) with 3% maleic anhydride-grafted polypropylene on the ...mechanical properties
of wood-plastic composites (WPCs). Polypropylene and fibers were compounded into pellets using a counter-rotating
twin-screw extruder and test specimens were prepared by injection molding. The results show that increases in fiber
length and fiber loading significantly increased (P < 0.05) the mechanical properties of the WPCs (MOE and tensile
modulus). The behavior of the composites against MOR and impact strength varied according to fiber length and loading
level. In general, the tensile strength was observed to be the same.
Beton non pasir merupakan jenis beton dengan porositas tinggi sehingga dapat dimanfaatkan untuk mempercepat penyerapan air hujan kedalam tanah. Penelitian ini terdapat dua uji, yakni uji infiltrasi ...dan kuat tekan beton tanpa pasir. Penelitian menggunakan 48 sampel untuk uji kuat tekan dan 16 sampel untuk uji infiltrasi dengan penambahan Sikamen-NN menggunakan variasi 0,8%, 1%, 1,2% serta 0,6% serat polipropilen terhadap berat semen. Agregat kasar menggunakan ukuran diameter lolos saringan ¾ tertahan pada saringan ½ 100% dan agregat kasar dengan ukuran diameter lolos saringan ½ tertahan saringan 100% yang berasal dari daerah Palu. Kemampuan terbesar infiltrasi beton non pasir adalah 41,80 mm/detik dan kuat tekan terbesar adalah 11,70 MPa dengan menggunakan agregat kasar ukuran diameter lolos saringan ½ tertahan saringan 100% ditambahkan dengan variasi Sikamen-NN 1,2%.
Analisis perubahan sifat termal polipaduan elastomer termoplastik-polietilen atau elastomer termoplastik- polipropilen akibat penambahan Karet Alam Cair (Liquid Natural Rubber/ LNR) telah dilakukan ...dengan teknik Simultaneous Thermal Analyzer (STA). Polipaduan LNR-polietilen dan LNR-polipropilen dilakukan dengan teknik blending dalam laboplastomill dengan variasi fraksi berat LNR sebesar 3 %berat, 5 %berat dan 7 %berat. Hasil karakterisasi dengan STA menunjukkan bahwa penambahan LNR 5 %berat pada polipaduan elastomer termoplastik-polietilen (ETP-PE) meningkatkan suhu puncak pelelehan dari ± 140 oC menjadi ± 164,1 oC, dan suhu mulai terjadinya dekomposisi meningkat dari ± 359 oC tanpa LNR menjadi ± 385 oC. Sedangkan polipaduan elastomer termoplastik-polipropilen meningkatkan suhu puncak pelelehan dari ± 170,4 0C menjadi ± 178,5 oC dan suhu mulai terjadinya dekomposisi meningkat dari ± 370,5 oC tanpa LNR menjadi ± 389,8 oC setelah penambahan LNR 3 %berat.
The aim of this study was to evaluate the potential utilization of fibre board waste generated from forest industry and furniture manufacturers in the production of wood plastic composite (WPC) for ...replacing wood flour. For production of WPC, polypropylene (PP) was chosen as polymer matrix, and eight different compositions were prepared with the co-rotating twin-screw extruder to compound them into pellets. WPC were produced at the size of 25 cm x 25 cm and 2 mm from these pellets (MDF flour loading varies 10 to 50 weight %) by hot press with the compression moulded technique according to ASTM D4703-10. For each composition, three composites were produced and ten specimens were prepared from these composites for tensile, flexural and notched impact specimens The tensile, flexural and impact properties of the manufactured samples were determined in accordance with ASTM D638, ASTM D6109, and ASTM D256, respectively. Morphological properties of the samples were characterized with scanning electron microscopy (SEM) analysis. Tensile and impact strength values decreased with increasing MDF flour loading whereas MOE values were improved with addition of MDF flour. All produced MDF flour filled composites showed better MOE and bending strength properties than ASTM D6662-13 standard requirements for polyolefin-based plastic lumber.Keywords: Wood plastic composites, Polypropylene, Medium density fiberboard flour
Bu çalışmada, orman endüstrisinin ve mobilya fabrikalarının üretim esnasında açığa çıkan lif levha atıklarının odun plastik kompozitlerin üretiminde odun unu yerine potansiyel olarak değerlendirilmesi hedeflenmiştir. Odun plastik kompozit (OPK) üretiminde polimer matris olarak polipropilen (PP) seçilmiş ve %10 ile %50 arasında lif levha atık unu ile sekiz farklı parametrede çift vidalı ekstrüder kullanılarak pellet üretimi gerçekleştirilmiştir. Üretilen pelletlerden 25 cm x 25 cm ve 2 mm ebatlarında ASTM D4703-10'a göre sıcak pres kalıplama tekniği yöntemiyle odun plastik kompozitler üretilmiştir. Her bir karışım parametresi için üç levha üretilmiş ve bunlardan on adet çekme, eğilme ve darbe direnç test örnekleri hazırlanmıştır. Hazırlanan örneklerin çekme, eğilme ve darbe dayanımı testleri sırası ile ASTM D638, ASTM D6109 ve ASTM256'ya göre tespit edilmiştir. Kopma yüzeyleri taramalı elektron mikroskobu (SEM) ile karakterize edilmiştir. MDF unu katılım oranının artmasına bağlı olarak çekme ve darbe direnç değerlerinde belirgin düşüşler gözlenmiştir. MDF unu takviyeli kompozitlerin elastikiyet modülü ve eğilme direnci değerleri plastik keresteler için ASTM D 6662 standardında istenen değerlerin çok üstünde olup plastik kereste kullanım alanlarında kullanılabileceği sonucuna ulaşılmıştır.Anahtar kelimeler: Odun plastik kompozitler, Polipropilen, Orta yoğunlukta lif levha unu
Günümüzde geleneksel betonlar kadar yüksek performanslı betonlar da kolaylıkla üretilebilmektedir. Betonların basınç dayanımının yüksek olması kadar, belli oranda sünek davranış göstermesi de ...istenmektedir. Bu amaçla, son yıllarda, sünekliği sağlayabilmek için üretimlerinde betonu liflerle takviye etmeye başlamışlar ve bu konuda da bir çok araştırma yapmışlardır. Bu liflerin başında çelik lifler gelmektedir. Bu çalışmada çelik ve polipropilen lif katkılı geleneksel ve yüksek dayanımlı betonlar üretilerek, bu betonların merkezi basınç, yarmada çekme dayanımları araştırılarak, çentikli numunelerde betonların kırılma ve çatlak gelişimleri incelenmiştir.
Today, high performance concrete can be produced as easily as normal strength concrete. Concretes are expected to have ductile behavior and have compressive strength, as well. In the recent years, in order to have ductile behavior, researchers have started to strengthen concrete using fibers and have done lots of researches. In this study, normal and high strength concrete with steel and polypropylene fiber are produced, the compressive strength and the tensile strength in split of these concrete is investigated and the fracture energy and crack distribution of notching samples are examined.
U radu je istražena potencijalna primjena lignoceluloznog punila u termoplastičnim kompozitima od biljke Vitex agnus-castus (konopljike), koja je listopadni invazivni grm. Stabljike konopljike ...promjera 5 – 10 cm nabavljene su iz grada Mugla, iz zapadne Turske. U polipropilensku matricu dodane su različite količine drvnog brašna (0 – 50 wt. %, uz povećanje od 10 %) koje je prolazilo kroz sito otvora 0,237 mm. Prethodno pomiješane sirovine stavljene su u lijevak dvovijčanog ekstrudera. Temperatura spremnika ekstrudera postupno je povećavana od 170 °C (zona uvlačenja) do 190 °C (zona istiskivanja), uz konstantnu brzinu vijka (40 okr./min). Zatim su osušene pelete 5 min vruće prešane pri 2 MPa i 190 °C u oblik WPC ploče debljine 4 mm. Kao kompatibilizator formulaciji je dodan MAPP (3 wt. %). Kako se količina punila u polipropilenu povećavala s 10 na 50 wt. %, kompoziti su pokazivali povećanje debljinskog bubrenja (od 0,58 do 5,68 %). S povećanjem količine čistoga drvnog brašna na 30 wt. %, čvrstoća na savijanje polipropilenskih kompozita povećala se s 33,9 na 44,8 MPa, ali daljnje je povećanje dovelo do smanjenja vlačne čvrstoće (25,7 MPa). Kada je udio drva dosegnuo 50 wt. %, modul savijanja povećao se s 815 na 3250 MPa. Pri povećanju udjela drva s 10 na 50 wt%, modul elastičnosti pri vlačnom se naprezanju povećao s 1690 na 2253 MPa. Utvrđeno je da su vlačna čvrstoća, modul elastičnosti pri vlačnom naprezanju, čvrstoća na savijanje i modul na savijanje polipropilena bez punila redom 19,6 MPa, 1505 MPa, 30,2 MPa i 664 MPa. Prema rezultatima ispitivanja, zaključeno je da se 30 – 40 wt. % drva konopljike može učinkovito iskoristiti u polipropilenskim kompozitima za primjenu u graditeljstvu kao što su podne ili zidne obloge. Istraživanje slabo iskorištene konopljike u proizvodnji WPC-a može rezultirati učinkovitim načinom upotrebe te sirovine.
The fly ash that is produced in the amount of up to 10 million tons annually in power stations in Turkey and waste polypropylene cause environmental pollution. In addition to environmental problems, ...the increasing demand for raw materials and limited availability of natural resources are the reasons to investigate fly ash and polypropylene wastes for their possible reuse. In this study, possible use of Soma Thermal Power Plant fly ash and propylene wastes in a new composite material was investigated. For this purpose, nine kinds of composite materials containing 10%-90% Soma thermal power plant fly ash were produced. Thermal conductivity, compressive strength, water absorption and abrasion tests were applied to investigate the mechanical and physical properties of the fabricated composite material specimens. In this application, these two waste materials can be utilized together, both to eliminate environmental problems and to get economical gains by saving energy.
U radu je istražen dugotrajni stupanj higroskopskoga debljinskog bubrenja polipropilenskih (PP) kompozita punjenih toplinski obrađenim drvnim brašnom. Iverje od bukovine bilo je toplinski tretirano ...na 120, 150 ili 180 °C tijekom 30 ili 120 minuta uz pomoć zasićene pare u digestoru. Kompoziti na bazi PP-a, brašna od bukovine (BF)-a i veziva (PP-g-MA) izrađeni su taljenjem i injekcijskim prešanjem. Maseni je omjer BF/PP za sve smjese bio 50/47. Količina veziva za sve formulacije bila je na 3 wt.%. Nadalje, provedeno je modeliranje debljinskog bubrenja kompozita i parametra brzine bubrenja (KSR). Debljinsko bubrenje uzoraka toplinski tretiranih 30 min na 120 ºC i 30 min na 150 ºC bilo je niže nego na kontrolnim uzorcima, zatim slijede uzorci toplinski tretirani 120 min na 180 ºC, 30 min na 180 ºC, 120 min na 120 ºC, odnosno 120 min na 150 ºC. Nadalje, debljinsko bubrenje BF/PP kompozita smanjivalo se s povećanjem vremena i temperature toplinskog postupka. Osim toga, kompoziti su pri 30 min na 120 ºC pokazali niži parametar brzine bubrenja od kontrolnih uzoraka. Na parametar brzine bubrenja kompozita utjecali su vrijeme toplinskog tretmana i temperatura.
Türkiye' de termik santrallerde yılda 10 milyon tonun üzerinde üretilen uçucu kül ve çevreye atılan polipropilen atıkları çevre kirliliğine neden olmaktadır. Yarattığı çevresel problemlerin yanında, ...hammadde kaynaklarına olan talebin hızla artması ve buna karşılık doğal kaynakların kısıtlı olması, uçucu küllerin ve atık polipropilenin yeniden kullanılabilirliğinin araştırılmasını gerekli kılmaktadır. Bu çalışmada, Soma Termik Santrali uçucu küllerinin ve polipropilen atıklarının yeni bir kompozit malzeme üretiminde kullanılabilirliği araştırılmıştır. Bu amaç ile % 10 - %90 hacim oranlarda Soma Termik Santrali uçucu külü içeren dokuz çeşit kompozit malzemelerin üretilmiştir. Üretilen kompozit numunelerin mekanik ve fiziksel özelliklerinin tespiti için ısıl iletkenlik, basma dayanımı, su emme kapasitesi, aşınma deneyleri yapılmıştır. Böyle bir uygulama ile, bu iki atık malzeme, hem çevre probleminin azaltılmasında hem de enerji tasarrufu yoluyla ekonomiye kazanç sağlanmasında değerlendirilebilecektir.
Türkiye' de termik santrallerde yılda 10 milyon tonun üzerinde üretilen uçucu kül ve çevreye atılan polipropilen atıkları çevre kirliliğine neden olmaktadır. Yarattığı çevresel problemlerin yanında, ...hammadde kaynaklarına olan talebin hızla artması ve buna karşılık doğal kaynakların kısıtlı olması, uçucu küllerin ve atık polipropilenin yeniden kullanılabilirliğinin araştırılmasını gerekli kılmaktadır. Bu çalışmada, Soma Termik Santrali uçucu küllerinin ve polipropilen atıklarının yeni bir kompozit malzeme üretiminde kullanılabilirliği araştırılmıştır. Bu amaç ile % 10 - %90 hacim oranlarda Soma Termik Santrali uçucu külü içeren dokuz çeşit kompozit malzemelerin üretilmiştir. Üretilen kompozit numunelerin mekanik ve fiziksel özelliklerinin tespiti için ısıl iletkenlik, basma dayanımı, su emme kapasitesi, aşınma deneyleri yapılmıştır. Böyle bir uygulama ile, bu iki atık malzeme, hem çevre probleminin azaltılmasında hem de enerji tasarrufu yoluyla ekonomiye kazanç sağlanmasında değerlendirilebilecektir.