Microstructure of Al-Mn-Be melt-spun ribbonsZupanič, Franc ...Microstructures of two alloys with the nominal compositions of Al92Mn3Be5 and Al89Mn6Be5 were characterized in the initial as-cast condition (after vacuum induction melting and casting) and after ... melt spinning. In the initial conditions, both alloys consisted of an aluminum-rich solid solution and two metastable intermetallic phases: Be4AlMn and Al10Mn3(Be). Both alloys melted over a rather large temperature range (between 230 °C and 310 °C). This was the main reason for the presence of unmelted particles in the melt-spun ribbons. Nonetheless, with the use of optimized melt-spinning parameters a microstructure composed of the Al-rich solid solution and finely dispersed quasicrystalline particles in ribbons with thicknesses ranging from 30-200 m was achieved. The dispersion of quasicrystalline particles was finest on the wheel side of the thinnest ribbons, attaining microhardness values between 250HV and 300 HV.Vir: Materials characterization. - ISSN 1044-5803 (Vol. 59, no 9, Sep. 2008, str. 1245-1251)Vrsta gradiva - članek, sestavni del ; neleposlovje za odrasleLeto - 2008Jezik - angleškiCOBISS.SI-ID - 11868950
Avtor
Zupanič, Franc |
Bončina, Tonica |
Šuštaršič, Borivoj |
Anžel, Ivan, inženir metalurgije in materialov |
Markoli, Boštjan
Teme
preiskava materialov |
litje na vrteče kovinsko kolo |
metalografija |
mikrostruktura |
aluminijeve zlitine |
trakovi |
kvazikristali |
kvazikristali |
melt spinning |
metallography |
microstructure |
aluminium alloys |
melt-spun ribbons |
quasicrystalls
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Zupanič, Franc | 12295 |
Bončina, Tonica | 14334 |
Šuštaršič, Borivoj | 08195 |
Anžel, Ivan, inženir metalurgije in materialov | 10369 |
Markoli, Boštjan | 16115 |
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.