Determination of shear bond strength between PEEK composites and veneering composites for the production of dental restorations [Elektronski vir]Kuchler, Anamarija ...We studied the shear bond strength (SBS) of two PEEK composites (BioHPP, BioHPP plus) with three veneering composites: Visio.lign, SR Nexco and VITA VM LC, depending on the surface treatment: ... untreated, sandblasted with 110 μm Al2O3, sandblasted and cleaned ultrasonically in 80% ethanol, with or without adhesive Visio.link, with applied Visio.link and MKZ primer. For the BioHPP plus, differential scanning calorimetry (DSC) revealed a slightly lower glass transition temperature (Tg 150.4 ± 0.4 °C) and higher melting temperature (Tm 339.4 ± 0.6 °C) than those of BioHPP (Tg 151.3 ± 1.3 °C, Tm 338.7 ± 0.2 °C). The dynamical mechanical analysis (DMA) revealed a slightly higher storage modulus of BioHPP (E’ 4.258 ± 0.093 GPa) than of BioHPP plus (E′ 4.193 ± 0.09 GPa). The roughness was the highest for the untreated BioHPP plus, and the lowest for the polished BioHPP. The highest hydrophobicity was achieved on the sandblasted BioHPP plus, whereas the highest hydrophilicity was found on the untreated BioHPP. The highest SBSs were determined for BioHPP and Visio.lign, adhesive Visio.link (26.31 ± 4.17 MPa) or MKZ primer (25.59 ± 3.17 MPa), with VITA VM LC, MKZ primer and Visio.link (25.51 ± 1.94 MPa), and ultrasonically cleaned, with Visio.link (26.28 ± 2.94 MPa). For BioHPP plus, the highest SBS was determined for a sandblasted surface, cleaned ultrasonically, with the SR Nexco and Visio.link (23.39 ± 2.80 MPa).Vir: Materials [Elektronski vir]. - ISSN 1996-1944 (Vol. 16, iss. 9, [article no.] 3286, April 2023, 18 str.)Vrsta gradiva - e-članek ; neleposlovje za odrasleLeto - 2023Jezik - angleškiCOBISS.SI-ID - 150518531
Avtor
Kuchler, Anamarija |
Pušnik Črešnar, Klementina |
Švab, Iztok |
Vuherer, Tomaž |
Žigon, Majda |
Brunčko, Mihael
Teme
CAD/CAM rezkanje |
stiskanje |
toplotni prehodi PEEK kompozitov |
hrapavost |
omočljivost |
trdnost strižne vezi |
BioHPP |
CAD/CAM milling |
BioHPP plus |
pressing |
veneering composites |
roughness |
wettability |
shear bond strength
Avtor | Kuchler, Anamarija ... |
Naslov | Determination of shear bond strength between PEEK composites and veneering composites for the production of dental restorations [Elektronski vir] |
Datum objave | 2023-04-22 |
COBISS.SI-ID | 150518531 |
Verzija objave v repozitoriju | Založnikova različica |
Licenca objave v repozitoriju | Creative Commons Priznanje avtorstva 4.0 Mednarodna |
Embargo | Takojšnja javna objava |
Projekti, iz katerih je bila financirana objava
Naziv | Akronim | Številka projekta | Financer |
---|---|---|---|
Tehnologije metastabilnih materialov | P2-0120-2022 |
Javna agencija za znanstvenoraziskovalno in inovacijsko dejavnost Republike Slovenije |
|
Tekstilna kemija in napredni tekstilni materiali | P2-0118-2022 |
Javna agencija za znanstvenoraziskovalno in inovacijsko dejavnost Republike Slovenije |
Datoteke, ki spadajo k objavi
Povezava |
---|
https://dk.um.si/IzpisGradiva.php?id=88003 |
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Kuchler, Anamarija | |
Pušnik Črešnar, Klementina | 34450 |
Švab, Iztok | 22426 |
Vuherer, Tomaž | 15682 |
Žigon, Majda | 06126 |
Brunčko, Mihael | 20229 |
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.