Senatore, E.V.; Pinto, M.C.P.; Souza, E.A.; Barker, R.; Neville, A.; Gomes, J.A.C. Ponciano
Wear, 09/2021, Letnik: 480-481Journal Article
In CO2 environments, an increase in the temperature can influence carbon steel flow-induced corrosion (FIC) and erosion-corrosion (EC) degradation processes. Increasing temperature typically results in the acceleration of electrochemical degradation mechanisms in the absence of protective corrosion product layers. Furthermore, the presence of sand in corrosive process fluids could aggravate the service conditions. Although protective iron carbonate (FeCO3) film or/and corrosion inhibitors are capable of suppressing corrosion in CO2-containing environments typical of oil and gas production, their ability to suppress degradation and their associated mechanisms in erosion-corrosion environments is less understood. This work focuses on understanding the ability of FeCO3 to protect the steel surface in the absence and presence of corrosion inhibitor and their interactions in flow-induced and erosion-corrosion systems at 60 °C. The effect of the temperature increase is investigated based on results obtained in a previous study performed at 25 °C. FeCO3 filmed carbon steel specimens were developed using an autoclave at 60 °C, pH 6.6 and 30 bar in a 1.5 wt% NaCl CO2-saturated solution over 48 h. The FeCO3 covered specimens were evaluated in FIC and EC environments at 60 °C and a flow velocity of 15 m/s in the presence and absence of 1000 mg/L sand and 100 ppm of a commercially available corrosion inhibitor. Results indicate that the sole presence of an FeCO3 layer is not sufficient to retard the corrosive process of carbon steel at 60 °C under EC conditions. However, the commercial corrosion inhibitor was observed to worked synergistically with the FeCO3 layer to reduce the corrosion degradation component in both the presence and absence of sand particles. The erosion component is also reduced in erosion-corrosion environments as a result of the combined presence of FeCO3 and corrosion inhibitor. •Inhibition action is maintained whether higher temperature.•Sole FeCO3 layer do not attenuate the corrosive process in EC tests.•Inhibitor and FeCO3 layer work synergistically reducing corrosion rate.•FeCO3 layer is not soluble at 60 °C within the operation window of FIC and EC tests.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.