Moreto, J.A.; Marino, C.E.B.; Bose Filho, W.W.; Rocha, L.A.; Fernandes, J.C.S.
Corrosion science, 07/2014, Letnik: 84Journal Article
•AA2198-T851 is a potential substitute for AA2524-T3 with higher pitting resistance.•AA7081-T73511 is more prone to pitting corrosion than the AA7050-T7451.•Cathodic Al7Cu2Fe particles promote dissolution of adjacent 7XXX matrix. The 2XXX and 7XXX series aluminium alloys are commonly used in aircraft applications where high strength-to-weight ratios are required. The present study aims to compare the corrosion resistance of two novel alloys developed for aircraft industry (AA2198-T851 and 7081-T73511) to that presented by the alternative base alloys (AA2524-T3 and 7050-T7451, respectively). Results indicate that AA2198-T851 may show a superior corrosion performance compared to AA2524-T3, being a potential candidate for its replacement, due to best mechanical properties. In what concerns the 7081-T73511, its resistance to pitting corrosion may be lower than for the base line alloy 7050-T7451.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.