Abbasi, Mehdi; Ahmadi, Farshid; Farzin, Mahmoud
Metals and materials international, 04/2021, Letnik: 27, Številka: 4Journal Article
The only problem of pure titanium for dental implant applications is its low strength and failure under different loadings. Various studies have shown that the utilization of severe plastic deformation processes such as Equal Channel Angular Pressing (ECAP), through reducing the grain size of titanium, can improve not only its mechanical properties but also its corrosion resistance and biocompatibility. In this study, a reduced-scale ECAP process on pure titanium was performed to investigate the effects of scale reduction. An ECAP die was made with an internal diameter of d = 3 mm, and the tests were performed at 250 °C for several number of passes. It was found out that after 10 passes of reduced-scale ECAP, the grain size of CP Ti had strongly been reduced from 25 to 122 nm. This sharp reduction in grain size resulted in an increase in micro-hardness from 205.5 to 321.3 Hv. Moreover, Nano-hardness test results showed that after 10 passes, the hardness of titanium increased from 2461 to 3812 MPa, and simultaneously elastic modulus decreased from 108.1 to 94.8 GPa. Such reduction of elastic modulus of titanium for dental implant applications decreased stress-shielding and jaw bone damages. According to the results of this research, after RS-ECAP process the strength of titanium is greatly increased and its elastic modulus is reduced, which are desirable features for dental implant applications. Since dental implants are small in size, the reduced ECAP process (d = 3–5 mm) can produce titanium implants with improved properties. Graphic Abstract
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.