Hirayama, Y.; Takahashi, Y.K.; Hirosawa, S.; Hono, K.
Scripta materialia, September 2017, Letnik: 138Journal Article
We have grown Sm(Fe1−xCox)12 (x=0, 0.1 and 0.2) films epitaxially on V(001) buffered MgO(001) single crystalline substrates in order to investigate the intrinsic hard magnetic properties of the Co substituted SmFe12 phase with the ThMn12 structure. We found Sm(Fe0.8Co0.2)12 has excellent intrinsic hard magnetic properties with spontaneous magnetization of 1.78T, anisotropy field of 12T and Curie temperature of 859K, all of which are superior to those for Nd2Fe14B. Hence, the Sm(Fe0.8Co0.2)12 compound is promising as permanent magnet material, if it can be stabilized in a bulk form. Display omitted
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.