Shamir, Muhammad; Zhang, Xiang; Syed, Abdul Khadar; Sadler, Wayne
Materials, 07/2023, Letnik: 16, Številka: 15Journal Article
This paper reports the effect of as-deposited surface conditions on the fatigue strength of an additively manufactured titanium alloy, Ti-6Al-4V (WAAM Ti64). First, the local stress concentration caused by the surface waviness was quantified using a metrology technique and computer modelling. Fatigue tests were conducted under bending loads at a cyclic load ratio of 0.1. The applicability of two predictive methods was the focus of this study. The traditional notch stress method was unable to predict the correct S-N curve trend slope, which could be attributed to the early crack initiation from the troughs on the as-built surface, with crack propagation being the dominant failure mechanism. By treating the troughs as small cracks, the fracture mechanics approach delivered good predictions at every applied stress level. Surface machining and polishing may not always be practical or required; it depends on the applications and service load levels. This research demonstrated that the fracture mechanics approach can be used for predicting the fatigue life of WAAM titanium alloys in as-built conditions and, hence, can be a tool for decision making on the level of surface machining.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.