Takagi, I.; Ueyama, Y.; Komura, T.; Akiyoshi, M.; Sasaki, T.; Moritani, K.; Moriyama, H.
Fusion science and technology, 11/2011, Letnik: 60, Številka: 4Journal Article
Type 304 stainless steel samples were irradiated with MeV-energy H and He ions and deuterium concentrations were in-situ observed by a nuclear reaction analysis (NRA) under a condition of continuous plasma exposure. It was found that one type of trap was produced by the irradiation and its trapping energy was 0.28 eV. The trap production rates to displacement were 6.8x10 -3 for He ion and 5.1x10 -4 for H ion, respectively. The trap was annihilated at 489 K in H-irradiated sample.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.