Schoenecker, Paul M; Carson, Cantwell G; Jasuja, Himanshu; Flemming, Christine J. J; Walton, Krista S
Industrial & engineering chemistry research, 05/2012, Letnik: 51, Številka: 18Journal Article
This work presents an experimental investigation of water adsorption in metal–organic frameworks (MOFs) at room temperature and up to 90% relative humidity. Structural degradation of the materials after regeneration is analyzed via powder X-ray diffraction (PXRD) and nitrogen adsorption measurements. MOFs with open metal sites are quite hydrophilic but appear to maintain their structure according to PXRD. However, significant surface area loss indicates that decomposition is occurring and is likely an attribute of oxygen presence during the regeneration procedure. Materials with copper paddle-wheel (HKUST-1), 5-coordinated magnesium (Mg MOF-74), and 7-coordinated zirconium (UiO-66(-NH2)) maintain good structural stability, while Zn-COOH containing MOFs (DMOF-1; DMOF-1-NH2; UMCM-1) undergo complete loss of crystallinity.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.