Dubois, G.; Volksen, W.; Magbitang, T.; Miller, R. D.; Gage, D. M.; Dauskardt, R. H.
Advanced materials (Weinheim), 11/2007, Letnik: 19, Številka: 22Journal Article
Mechanical properties of organic/ inorganic thin‐films prepared from bridged silicon precursors have been investigated. The Young's modulus follows a linear decay when porosity is introduced, a unique observation as compared to traditional organosilicates. Remarkably, in the dense state, fracture energies of 15–17 J.m–2 were measured, values that are larger than those for dense SiO2 (10 J.m–2), dispelling the common belief that all organosilicates are fragile and prone to fracture.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.