Wharton, J.A; Wood, R.J.K
Wear, 03/2004, Letnik: 256, Številka: 5Journal Article
Hydrodynamic and electrochemical noise measurements (ENMs), of AISI 304L stainless steel, were made in a pipe test section of 28 mm inside diameter for a range of flow regimes from laminar to turbulent. Mean flow velocities through the test section were controlled at 0.04, 0.07, 0.11, 0.36, 1.8 and 2.7 m s −1, equivalent to Reynolds numbers of 1000, 2000, 3000, 10 000, 50 000 and 75 000, respectively. Standard hydrodynamic parameters were employed to characterise and evaluate the complex interrelationship between the mass transfer rate of oxygen and momentum transfer through turbulence to the metal/solution interface. For AISI 304L stainless steel, pitting typically occurs in the form of metastable pits which either repassivated before achieving stability or grow to become stable pits. Metastable pitting was evident under all flow regimes. The fluid flow, whether laminar or turbulent, had little overall effect on the nucleation rates of metastable pitting events. Conversely, stable pit growth was most evident during laminar flow immediately before the transition to turbulent flow and close to the critical velocity (∼1.5 m s −1).
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.