Wang, Y.Q.; Duan, R.H.; Hu, J.; Luo, Z.A.; Ma, Z.Y.; Xie, G.M.
Journal of materials processing technology, August 2022, 2022-08-00, 20220801, Letnik: 306Journal Article
The medium-Mn steels have a great application potential in the engineering fields due to its excellent strength and toughness. However, the presence of coarse martensite and segregation of Mn in the fusion-welded medium-Mn steel joint severely deteriorated toughness and ductility. In this work, 6 mm thick medium-Mn steel plates were joined by friction stir welding, and then were intercritically annealed to enhance the toughness and ductility of the joint. The as-welded nugget zone (NZ) contained lath martensite with low proportion of high angle boundaries (HABs), leading to the joint with lower elongation of 22.5% and the impact energy of 73.6 J/cm2. However, the as-annealed NZ consisted of ferrite and austenite because partial martensite changed to reversed austenite, while other martensite became ferrite during annealing. In addition, the proportion of HABs in the as-annealed NZ increased obviously. In comparison with as-welded joint, the impact energy and elongation of the as-annealed joint was increased by 70.7% and 44.4%, respectively. The abovementioned excellent mechanical properties were attributed to the high proportion of HABs and a large amount of ultra-fine reversed austenite with high thermal and mechanical stability, which provided a significant transformation induced plasticity effect, obviously inhibiting crack initiation and propagation. This systematic work provided a reference for welding similar materials containing retained austenite.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.