Lopes, V.; Puga, H.; Gomes, I.V.; Peixinho, N.; Teixeira, J.C.; Barbosa, J.
Journal of materials processing technology, January 2022, 2022-01-00, 20220101, Letnik: 299Journal Article
The present study addresses a thin-walled investment casting methodology of AZ91D-1 wt% CaO magnesium alloy for stent manufacturing. Additive manufacturing and Yttria-based coating were applied to optimize the process. An induction melting furnace assisted by vacuum was used to cast magnesium alloy stents with 0.4 mm and 0.8 mm wall thickness under an argon-protective atmosphere. According to the proposed methodology and the results obtained for coated models, no metal-mould interface reactions were found, revealing samples with a good surface finish and sane microstructure. The cast magnesium stents without coating were compromised, resulting in samples with a high degree of reactions and impurities. Microscopic examination and hardness measurements demonstrated the effectiveness of the process.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.