Xin, Yunchang; Wang, Maoyin; Zeng, Zhen; Huang, Guangjie; Liu, Qing
Scripta materialia, 05/2011, Letnik: 64, Številka: 10Journal Article
► Pr-rolling along TD initiates (10–12) twins which incline basal plane by 86°. ► Inclination of basal plane can effectively improve rolling capability at 300 °C. ► Non-basal slip of 〈a〉 dislocation in pre-rolled sample can accommodate strain in ND. A method to weaken the strong basal texture of rolled magnesium alloy by twinning deformation is reported. Pre-rolling along the transverse direction at room temperature initiates extension twinning and reorients the basal plane. A dramatically increased maximum thickness reduction per pass during subsequent rolling at 300 °C is achieved in pre-deformed sample compared to that of the directly rolled one. The corresponding mechanisms are addressed and discussed.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.