Yao, Lu; Li, Yugui; Song, Yaohui; Sun, Haosong; Lu, Yibo; Wang, Jiayao
Materiali in tehnologije, 01/2023, Letnik: 57, Številka: 6Journal Article
We have studied the effects of different solution temperatures and holding times on the microstructure and room-temperature mechanical properties of the alloy using methods such as electron backscatter diffraction, hardness testing and tensile testing. The results showed that the average grain size increased significantly as the solution temperature increased, and many annealing twins appeared in the grains. The fraction of twin boundaries reached its maximum value at 1080 °C. The hardness, yield strength and tensile strength of the alloy decreased with an increase in the solution temperature, but abnormal yielding occurred at 1160 °C. The elongation after fracture and the area reduction increased with an increase in the solution temperature. The fracture morphology of the alloy was irregular, conical, accompanied by a large number of ductile dimples, and the material exhibited typical ductile fracture. At the same time, as the solution temperature increased, the number of dimples on the fracture surface continued to increase, the depth of the dimples gradually increased, and the distribution became more uniform.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.