Mortazavi, Nooshin; Bonora, Nicola; Ruggiero, Andrew; Hörnqvist Colliander, Magnus
Metallurgical and materials transactions. A, Physical metallurgy and materials science, 06/2016, Letnik: 47, Številka: 6Journal Article
Discontinuous dynamic recrystallization can occur during dynamic tensile extrusion of copper, which is subjected to uniaxial tensile strains of ~5 and strain rates up to 10 6 s −1 in the extruded section. Through high-resolution transmission Kikuchi diffraction, we show that nucleation occurs through subgrain rotation and grain boundary bulging at boundaries between 〈001〉 and 〈111〉 oriented grains. The observed nuclei consist of subgrains with a size of approximately 200 to 400 nm.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.