Deng, Zongyi; Lv, Yunfei; Shi, Minxian; Huang, Zhixiong; Huang, Wenchao
Polymers, 11/2023, Letnik: 15, Številka: 22Journal Article
Hypersonic vehicles encounter hostile service environments of thermal/mechanical/chemical coupling, so thermal protection materials are crucial and essential. Ceramizable composites have recently attracted intensive interest due to their ability to provide large-area thermal protection for hypersonic vehicles. In this work, a novel ceramizable composite of quartz fiber/benzoxazine resin modified with fused SiOsub.2 and h-BN was fabricated using a prepreg compression molding technique. The effects of the fused SiOsub.2 and h-BN contents on the thermal, mechanical, and ablative properties of the ceramizable composite were systematically investigated. The ceramizable composite with an optimized amount of fused SiOsub.2 and h-BN exhibited superb thermal stability, with a peak degradation temperature and residue yield at 1400 °C of 533.2 °C and 71.5%, respectively. Moreover, the modified ceramizable composite exhibited excellent load-bearing capacity with a flexural strength of 402.2 MPa and superior ablation resistance with a linear ablation rate of 0.0147 mm/s at a heat flux of 4.2 MW/msup.2, which was significantly better than the pristine quartz fiber/benzoxazine resin composite. In addition, possible ablation mechanisms were revealed based on the microstructure analysis, phase transformation, chemical bonding states, and the degree of graphitization of the ceramized products. The readily oxidized pyrolytic carbon (PyC) and the SiOsub.2 with a relatively low melting point were converted in situ into refractory carbide. Thus, a robust thermal protective barrier with SiC as the skeleton and borosilicate glass as the matrix protected the composite from severe thermochemical erosion and thermomechanical denudation.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.