Zhong, Wen; Chen, Siqiang; Ma, Lei; Tong, Zhe
Materials, 11/2022, Letnik: 15, Številka: 22Journal Article
Hybrids of fluorinated graphite/MoSsub.2 (FGr@MoSsub.2) were prepared via a hydrothermal method and used as lubricating additives to take full advantage of the synergy between FGr and MoSsub.2 in carbon-fiber-reinforced polymer (CFRP). The results show a 21.6% reduction in the friction coefficient compared to the neat sample when the CFRP was filled with 1.2 wt.% FGr@MoSsub.2 hybrids. The addition of 1.5 wt.% FGr@MoSsub.2 resulted in a 60.9% reduction in the wear rate compared to neat CFRP. For the 1.2 wt.% FGr@MoSsub.2-reinforced CFRP, the friction coefficient maintained a relatively steady value of approximately 0.46 at various temperatures, indicating frictional stability. However, the wear rate increased by 13.95% at 60 °C compared to that at room temperature. The interfacial bonding force between the FGr@MoSsub.2 hybrid and the matrix, as well as the adhesive force with the surface of the counterpart ball, is improved, caused by the heterostructure of FGr@MoSsub.2, resulting in enhanced mechanical properties and formation efficiency as well as the transfer film on the surface of the counterpart ball. The results suggest that an FGr@MoSsub.2 micro-nano structure is a promising additive to be applied in polymer tribology.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.