Horbach, Lutz; Zhang, Jiali; Sedlatschek, Tobias; Weber, Felix; Gebhardt, Christian; David Joseph, Betto; Bührig-Polaczek, Andreas; Broeckmann, Christoph
Materials & design, August 2024, 2024-08-00, 2024-08-01, Letnik: 244Journal Article
Display omitted •Measurement of silicon segregation in solution strengthened ferritic ductile iron.•Micropillar compression tests and trace analysis.•Determination of CRSS as a function of the silicon content in the ferrite matrix.•Comparison of the measured CRSS with macroscopic yield limits under tension and compression. Solid solution strengthened ferritic ductile iron (SSFDI) exhibits improved mechanical properties compared to conventional ductile cast iron (DCI) grades, however, its potential widespread application is hindered by unpredictable brittle fracture which might be attributed to microstructural silicon segregation and associated superstructure formation. The aim of the present study is therefore to deepen the understanding on the effect of local silicon segregation on the mechanical properties of SSFDI, which is crucial especially for the common applications of DCI in cyclically loaded structures. Micropillar compression tests were carried out on three different casts to investigate the solution strengthening effect of silicon in the ferritic matrix. An almost perfect linear relationship between critical resolved shear stress (CRSS) and global silicon content was found. It was also found that the variation of CRSS with silicon content corresponds well to the variation of the macroscopic yield limits (under tension and compression) with global silicon content of different SSFDI alloys. This indicates that the ferritic matrix dominates the yield limit of the DCI alloys investigated in this study, while the morphology of the graphite nodules plays a minor role under monotonic loading conditions.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.