Ordered surface nanostructures have attracted much attention in biotechnology and biomedical engineering because of their potential to modulate cell-surface interactions in a controllable manner. ...However, the ability to fabricate large area ordered nanostructures is limited because of high costs and low speed of fabrication. Here, we have fabricated ordered nanostructures with large surface areas (1.5 × 1.5 cm(2)) using a combination of facile techniques including colloidal self-assembly, colloidal lithography and glancing angle deposition (GLAD). Polystyrene (722 nm) colloids were self-assembled into a hexagonally close-packed (hcp) crystal array at the water-air interface, transferred on a biocompatible tantalum (Ta) surface and used as a mask to generate an ordered Ta pattern. The Ta was deposited by sputter coating through the crystal mask creating approximately 60-nm-high feature sizes. The feature size was further increased by approximately 200-nm-height respectively using GLAD, resulting in the fabrication of four different surfaces (FLAT, Ta60, GLAD100, and GLAD200). Cell adhesion, proliferation, and osteogenic differentiation of primary human adipose-derived stem cells (hADSCs) were studied on these ordered nanostructures for up to 2 weeks. Our results suggested that cell spreading, focal adhesion formation, and filopodia extension of hADSCs were inhibited on the GLAD surfaces, while the growth rate was similar between each surface. Immunostaining for type I collagen (COL1) and osteocalcin (OC) showed that there was higher osteogenic components deposited on the GLAD surfaces compared to the Ta60 and FLAT surfaces after 1 week of osteogenic culture. After 2 weeks of osteogenic culture, alkaline phosphatase (ALP) activity and the amount of calcium was higher on the GLAD surfaces. In addition, osteoblast-like cells were confluent on Ta60 and FLAT surfaces, whereas the GLAD surfaces were not fully covered suggesting that the cell-cell interactions are stronger than cell-substrate interactions on GLAD surfaces. Visible extracellular matrix deposits decorated the porous surface can be found on the GLAD surfaces. Depth profiling of surface components using a new Ar cluster source and X-ray photoelectron spectroscopy (XPS) showed that deposited extracellular matrix on GLAD surfaces is rich in nitrogen. The fabricated ordered surface nanotopographies have potential to be applied in diverse fields, and demonstrate that the behavior of human stem cells can be directed on these ordered nanotopographies, providing new knowledge for applications in biomaterials and tissue engineering.
Dense, ultrathin networks of isocyanate terminated star-shaped poly(ethylene oxide) (PEO) molecules, cross-linked at their chain ends via urea groups, were shown to be extremely resistant to ...unspecific adsorption of proteins while at the same time suitable for easy biocompatible modification. Application by spin coating offers a simple procedure for the preparation of minimally interacting surfaces that are functionalized by suitable linker groups to immobilize proteins in their native conformations. These coatings form a versatile basis for biofunctional and biomimetic surfaces. We have demonstrated their advantageous properties by using single-molecule fluorescence microscopy to study immobilized proteins under destabilizing conditions. Biotinylated ribonuclease H (RNase H) was labeled with a fluorescence resonance energy transfer (FRET) pair of fluorescent dyes and attached to the surface by a biotin-streptavidin linkage. FRET analysis demonstrated completely reversible denaturation/renaturation behavior upon exposure of the surface-immobilized proteins to 6 M guanidinium chloride (GdmCl) followed by washing in buffer. A comparison with bovine serum albumin (BSA) coated surfaces and linear PEO brush surfaces yielded superior performance in terms of chemical stability, inertness and noninteracting nature of the star-polymer derived films.
This study presents the easy and fast patterning of low molecular weight molecules that act as binding partners for proteins on Star PEG coatings. These coatings are prepared from isocyanate ...terminated star shaped prepolymers and form a highly cross-linked network on the substrate in which the stars are connected via urea groups and free amino groups are present. Streptavidin has been patterned on these layers by microcontact printing (muCP) of an amino reactive biotin derivative and consecutive binding of streptavidin to the biotin. Patterns of Ni(2+)-nitriltriacetic acid (NTA) receptors have been prepared by printing amino functional NTA molecules in freshly prepared Star PEG layers that still contain amino reactive isocyanate groups. Complexation of the NTA groups with Ni(II) ions enabled the binding of His-tag enhanced green fluorescent protein (EGFP) in the desired pattern on the substrates. Since the unmodified Star PEG layers prevent unspecific protein adsorption, His-EGFP could selectively be bound to the sample by immersion into crude, nonpurified His-tag EGFP containing cell lysate.
Background
The ability to present signalling molecules within a low fouling 3D environment that mimics the extracellular matrix is an important goal for a range of biomedical applications, both
in ...vitro
and
in vivo
. Cell responses can be triggered by non-specific protein interactions occurring on the surface of a biomaterial, which is an undesirable process when studying specific receptor-ligand interactions. It is therefore useful to present specific ligands of interest to cell surface receptors in a 3D environment that minimizes non-specific interactions with biomolecules, such as proteins.
Method
In this study, surface-initiated atom transfer radical polymerization (SI-ATRP) of poly(ethylene glycol)-based monomers was carried out from the surface of electrospun fibers composed of a styrene/vinylbenzyl chloride copolymer. Surface initiated radical addition-fragmentation chain transfer (SI-RAFT) polymerisation was also carried out to generate bottle brush copolymer coatings consisting of poly(acrylic acid) and poly(acrylamide). These were grown from surface trithiocarbonate groups generated from the chloromethyl styrene moieties existing in the original synthesised polymer. XPS was used to characterise the surface composition of the fibers after grafting and after coupling with fluorine functional XPS labels.
Results
Bottle brush type coatings were able to be produced by ATRP which consisted of poly(ethylene glycol) methacrylate and a terminal alkyne-functionalised monomer. The ATRP coatings showed reduced non-specific protein adsorption, as a result of effective PEG incorporation and pendant alkynes groups existing as part of the brushes allowed for further conjugation of via azide-alkyne Huisgen 1,3-dipolar cycloaddition. In the case of RAFT, carboxylic acid moieties were effectively coupled to an amine label via amide bond formation. In each case XPS analysis demonstrated that covalent immobilisation had effectively taken place.
Conclusion
Overall, the studies presented an effective platform for the preparation of 3D scaffolds which contain effective conjugation sites for attachment of specific bioactive signals of interest, as well as actively reducing non-specific protein interactions.
An invisible surface: Single protein molecules were immobilized on a cross‐linked polymer surface (see cartoon), and imaged using fluorescence resonance energy transfer (FRET). The surface not only ...maintained the correct conformation of the protein molecules, but also allowed them to be unfolded and refolded fifty times consecutively. Moreover, the measured δG, cooperativity and the transition midpoint in guanidinium chloride of the unfolding‐folding transition on the surface was identical to the protein in solution. Thus, the surface is energetically ‘invisible’ to the folding protein.
In this study, star PEG coatings on glass substrates have been used as support material for oligonucleotide microarrays. These coatings are prepared from solutions of six armed star shaped ...prepolymers that carry reactive isocyanate endgroups. As described earlier, such films prevent the adsorption of proteins and the adhesion of cells but can easily be functionalized for specific biological recognition. Here we used the high functionality of these coatings for the covalent immobilization of amino terminated 20mer oligonucleotides, both by microcontact printing and spotting techniques. The permanent immobilization of fluorescently labeled DNA as well as hybridization of 20mer oligonucleotides have been monitored by fluorescence microscopy. The hybridization efficiency as determined by fluorescence intensity varied from 30% to 80% depending on the way of layer preparation. The direct spotting without additional activation and blocking steps of the surface demonstrates the potential of star PEG coatings as ultrathin surface modification for microarrays.