Different types of microfibrillated cellulose (MFC) and fines suspensions were produced, characterized, and then added to a papermaking pulp suspension. High and medium molar mass cationic ...polyelectrolytes were used as fixatives. The drainage behavior of the pulp suspensions with additives were evaluated against the strength properties of hand sheets made thereof. The effects of salt concentration, pH, fixative type, dosage and type of fibrillar material on drainage were examined. All the MFC and fines samples produced had clearly different properties due to their dissimilar production methods, and they also introduced specific responses on the measured drainage and paper strength. Generally, the addition of MFC decreased the drainage rate of pulp suspension and increased the strength of paper. However, it was shown that by optimum selection of materials and process conditions an enhancement of the strength properties could be achieved without simultaneously deteriorating the drainage.
Despite the structural, load‐bearing role of cellulose in the plant kingdom, countless efforts have been devoted to degrading this recalcitrant polysaccharide, particularly in the context of biofuels ...and renewable nanomaterials. Herein, we show how the exposure of plant‐based fibers to HCl vapor results in rapid degradation with simultaneous crystallization. Because of the unchanged sample texture and the lack of mass transfer out of the substrate in the gas/solid system, the changes in the crystallinity could be reliably monitored. Furthermore, we describe the preparation of cellulose nanocrystals in high yields and with minimal water consumption. The study serves as a starting point for the solid‐state tuning of the supramolecular properties of morphologically heterogeneous biological materials.
Vapor over the cracks: The adsorption of hydrogen chloride vapor on water‐covered cellulose microfibrils results in rapid degradation and increased crystallinity without a change in fiber morphology. This process constitutes an example of supramolecular tuning of native biological materials directly in the solid state.
► Empty Palm Fruit Bunch Fibers (EPFBF) were subject to sulfur-free chemical treatments. ► Microfluidization of EPFBF yields nanofibrils comparable to those from wood fibers. ► Nanopaper with ...excellent properties was manufactured from nanofibrillar EPFBF. ► Valorization of EPFBF is attractive due its higher yields and lower costs.
Different cellulose pulps were produced from sulfur-free chemical treatments of Empty Palm Fruit Bunch Fibers (EPFBF), a by-product from palm oil processing. The pulps were microfluidized for deconstruction into nanofibrillated cellulose (NFC) and nanopaper was manufactured by using an overpressure device. The morphological and structural features of the obtained NFCs were characterized via atomic force and scanning electron microscopies. The physical properties as well as the interactions with water of sheets from three different pulps were compared with those of nanopaper obtained from the corresponding NFC. Distinctive chemical and morphological characteristics and ensuing nanopaper properties were generated by the EPFBF fibers. The NFC grades obtained compared favorably with associated materials typically produced from bleached wood fibers. Lower water absorption, higher tensile strengths (107–137MPa) and elastic modulus (12–18GPa) were measured, which opens the possibility for valorization of such widely available bioresource.
Developing sustainable chemical methods to synthesize silver nanoparticles has drawn significant research interest. Due to their unique and well-defined physical-chemical properties, cellulose ...nanocrystals (CNCs) have become one of the most promising renewable nanomaterials. Here we use CNC to mediate silver nanoparticle synthesis and elucidate the effect of CNC surface chemistry (as defined by sulfate groups) in nanoparticle formation and nucleation in the presence of borohydride reduction. Pristine CNCs produced by sulfuric acid hydrolysis and partially desulfated CNCs mediated the formation of silver nanoparticles of different sizes (and size distribution) following different rates of formation, as determined by transmission electron microscopy (TEM) and UV-vis spectroscopy. The results shed light on methods to stabilize silver nanoparticles, control their nucleation, and highlight the potential of CNCs in metal nanoparticle synthesis.
The adsorption of human immunoglobulin G (hIgG) and bovine serum albumin (BSA) on cellulose supports were investigated. The dynamics and extent of related adsorption processes were monitored by ...surface plasmon resonance (SPR) and quartz crystal microbalance with dissipation monitoring (QCM-D). Amine groups were installed on the cellulose substrate by adsorption of chitosan from aqueous solution, which allowed for hIgG to physisorb from acid media and produced a functionalized substrate with high surface density (10 mg/m(2)). hIgG adsorption from neutral and alkaline conditions was found to yield lower adsorbed amounts. The installation of the carboxyl groups on cellulose substrate via carboxymethylated cellulose (CMC) adsorption from aqueous solution enhanced the physisorption of hIgG at acidic (adsorbed amount of 5.6 mg/m(2)) and neutral conditions. hIgG adsorption from alkaline conditions reduced the surface density. BSA was used to examine protein attachment on cellulose after modification with chitosan or carboxymethyl cellulose. At the isoelectric point of BSA (pI 5), both of the surface modifications enhanced the adsorption of this protein when compared to that on unmodified cellulose (a 2-fold increase from 1.7 to 3.5 mg/m(2)). At pH 4, the electrostatic interactions favored the adsorption of BSA on the CMC-modified cellulose, revealing the affinity of the system and the possibility of tailoring biomolecule binding by choice of the surface modifier and pH of the medium.
Cellulose nanocrystals (CNCs) or nanowhiskers produced from sulfuric acid hydrolysis of ramie fibers were used as substrates for surface chemical functionalization with thermoresponsive ...macromolecules. The CNCs were grafted with poly(N-isopropylacrylamide) brushes via surface-initiated single-electron transfer living radical polymerization (SI-SET-LRP) under various conditions at room temperature. The grafting process was confirmed via Fourier transform IR spectroscopy and X-ray photoelectron spectroscopy and the different molecular masses of the grafts were quantified and found to depend on the initiator and monomer concentrations used. No observable damage occurred to the CNCs after grafting, as determined by X-ray diffraction. Size exclusion chromatography analyses of polymer chains cleaved from the cellulose nanocrystals indicated that a higher degree of polymerization was achieved by increasing initiator or monomer loading, most likely caused by local heterogeneities yielding higher rates of polymerization. It is expected that suspension stability, interfacial interactions, friction, and other properties of grafted CNCs can be controlled by changes in temperature and provide a unique platform for further development of stimuli-responsive nanomaterials.
Unbleached (UN), oxygen-delignified and fully-bleached (FB) birch fibers with a residual lignin content of ca. 3, 2 and <1 %, respectively, were used to produce nanofibrillated cellulose (NFC) and ...nanopaper by using an overpressure device. The tensile index, elongation and elastic modulus of nanopaper were compared and the effect of residual cell wall components accessed. Under similar manufacturing conditions, UN NFC produced nanopaper with a density of 0.99 g/cm
3
, higher than that from FB NFC (0.7 g/cm
3
). This translated in much lower air permeability in the case of UN nanopaper (1 and 11 mL/min for UN and FB samples, respectively). Fundamentally, these observations are ascribed to the finer fibrils produced during microfluidization of UN fibers compared to those from lower yield counterparts (AFM roughness of 8 and 17 nm and surface areas of 124 and 98 m
2
/g for NFC from UN and FB fibers, respectively). As a result, values of stress at break and energy absorption of nanopaper from high yield fibers are distinctively higher than those from fully bleached NFC. Interactions of water with the surface and bulk material were affected by the chemical composition and structure of the nanofibrils. While UN nanopaper presented higher water contact angles their sorption capacity (and rate of water absorption) was much higher than those measured for nanopaper from FB NFC. These and other observations provided in this contribution are proposed to be related to the mechanoradical scavenging capacity of lignin in high shear microfluidization and the presence of residual heteropolysaccharides.
Display omitted
► Systematic comparison of different cellulose nanofibrils in multilayer formation. ► Nonelectrostatic interactions were decisive in build-up of cellulosic multilayers. ► Native, ...unmodified NFC was also successfully used in multilayers. ► The underlying cationic layer affected the interactions between NFC fibrils.
The multilayer formation between polyelectrolytes of opposite charge offers possibility for creating new tailored materials. Exchanging one or both components for charged nanofibrillated cellulose (NFC) further increases the variety of achievable properties. We explored this by introducing unmodified, low charged NFC and high charged TEMPO-oxidized NFC. Systematic evaluation of the effect of both NFC charge and properties of cationic polyelectrolytes on the structure of the multilayers was performed. As the cationic component cationic NFC was compared with two different cationic polyelectrolytes, poly(dimethyldiallylammoniumchloride) and cationic starch. Quartz crystal microbalance with dissipation (QCM-D) was used to monitor the multilayer formation and AFM colloidal probe microscopy (CPM) was further applied to probe surface interactions in order to gain information about fundamental interactions and layer properties. Generally, the results verified the characteristic multilayer formation between NFC of different charge and how the properties of formed multilayers can be tuned. However, the strong nonelectrostatic affinity between cellulosic fibrils was observed. CPM measurements revealed monotonically repulsive forces, which were in good correspondence with the QCM-D observations. Significant increase in adhesive forces was detected between the swollen high charged NFC.