Cui, Yu-Wei; Chen, Liang-Yu; Qin, Peng; Li, Ruifeng; Zang, Qianhao; Peng, Jinhua; Zhang, Lina; Lu, Sheng; Wang, Liqiang; Zhang, Lai-Chang
Corrosion science, 07/2022, Volume: 203Journal Article
The metastable pitting corrosion behavior of laser powder bed fusion (LPBF) produced Ti-6Al-4V is still unclear. Therefore, this work investigated the metastable pitting corrosion of LPBF-produced Ti-6Al-4V in Hank’s solution by electrochemical methods. The LPBF-produced sample (dominant by α′ phase in the microstructure) shows a higher frequency of pit nucleation than the annealed counterpart (composed by α + β dual phase). The passive films formed on the LPBF-produced sample exhibit a higher flux of oxygen vacancies, resulting in the absorption of more aggressive ions (e.g., Cl-) thereby producing more cation vacancies. The condensation of excessive cation vacancies contributes to the pit nucleation. Display omitted •Laser powder bed fusion (LPBF) produced Ti–6Al–4 V alloy was used as the sample.•Corrosion behavior of the LPBF-produced sample was investigated in Hank’s solution.•The LPBF-produced Ti-6Al-4 V shows frequent metastable pitting corrosion.•The flux of oxygen vacancy is large in the passive film of LPBF-produced Ti-6Al-4 V.•Redundant vacancies assemble and condense into a void at metal/film interface.
Author
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.