Sultana, Jolaikha; Sawon, Asraf; Brzykcy, Grace; Pathak, Arjun K.; Mishra, Sanjay R.
AIP advances, 02/2024, Volume: 14, Issue: 2Journal Article
Aluminum-doped ErCr1-xAlxO3 orthochromites prepared via autocombustion technique were investigated for their magnetic and magnetocaloric properties. X-ray diffraction confirmed that samples were orthorhombic phases with the Pbnm space group without a trace of any impurity. As analyzed via Rietveld refinement of XRD data, structural parameters such as lattice parameters, volume, bond angle, and bond lengths were affected by doping nonmagnetic Al3+ in the compound. ErCrO3 possesses the long-range antiferromagnetic ordering with a weak display ferromagnetism at TN =133 K. Low-temperature high-field magnetic study shows a decrease in Neel temperature (TN ∼ 114 K for x = 0.5), suggesting magnetic ordering suppression due to Al3+ doping. The asymptotic paramagnetic Curie temperature Tcw = −25 K suggests the predominance of antiferromagnetic interactions in ErCrO3 orthochromites, which was observed to increase with Al3+ doping. Isothermal magnetization data show changes in magnetic entropy (−ΔSMmax) and relative cooling power (RCP). The magnetic entropy change, −ΔSMmax, for ErCrO3 estimated from magnetization measurements show 11.60 J kg−1 K−1 at 11 K and a relative cooling power (RCP) of 209.4 J kg−1 at 5 T applied field. While ErCr0.75Al0.25O3 show a maximum magnetic entropy of 11.52 J kg−1 K−1 at 11 K with a 5 T applied field and RCP of 186.66 J kg−1, whereas ErCr0.5Al0.5O3 displayed −ΔSMmax of 11.63 J kg−1 K−1 at 5 K with a 5 T applied field and RCP value of 160.78 J kg−1. The results show that nonmagnetic doping, such as Al3+, could maintain the compound’s magnetocaloric property to an extent.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.