Liu, Yong; Zhang, Xuefeng; Dong, Shangli; Ye, Zhuyu; Wei, Yidan
Journal of materials science, 02/2017, Volume: 52, Issue: 4Journal Article
The highly exfoliated Ti.sub.3C.sub.2T.sub.x nanosheets were synthesized by selective etching of the starting material of Ti.sub.3AlC.sub.2 using 40 % concentrated HF solution at 65 °C for 5 h. The effect of HF treatment temperature on the exfoliation degree was investigated by characterizing the morphology and microstructure of the Ti.sub.3C.sub.2T.sub.x nanosheets using SEM, XRD, and TEM. The results showed that the exfoliation degree of Ti.sub.3C.sub.2T.sub.x was increased with increasing temperature. The role of the termination groups produced during HF treatment on the exfoliation degree was discussed. The tribological property of the prepared Ti.sub.3C.sub.2T.sub.x nanosheets as additives in PAO8 base oil was measured. The maximum reduction of friction and wear was achieved under additive concentration of 0.8 wt% for the highly exfoliated Ti.sub.3C.sub.2T.sub.x nanosheets. The different effects of Ti.sub.3C.sub.2T.sub.x additives on the average friction coefficient and wear volume were analyzed, respectively.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.