Comprehensive evaluation of electrocaloric effect and fatigue behavior in the 0.9Pb(Mg1/3Nb2/3)O3-0.1PbTiO3 bulk relaxor ferroelectric ceramicDel Duca, Manuel Gesù ...Electrocaloric refrigeration shows potential as a viable alternative to vapor-compression and/or thermo-electric refrigeration. One of the main challenges that need to be addressed in electrocaloric ... technology is the fatigue behavior of electrocaloric materials, in terms of both structural and functional aspects. Here, a comprehensive evaluation of the fatigue behavior of the 0.9Pb(Mg1/3Nb2/3)O3-0.1PbTiO3 (PMN-10PT) bulk relaxor ferroelectric (or shortly relaxor) ceramic at room temperature is performed. First, the temperature-change dependence on the slew rate was studied. It is shown that the adiabatic conditions are well approached at the slew rate above 1 kVs-1, at which the adiabatic temperature change of 1.3 K was measured at the electric field change of 90 kVcm-1. Then, the durability limits (i.e., the fatigue life) of ten PMN-10PT samples were investigated during unipolar electric field cycling. The results showed that the material could withstand up to 106 cycles at the electric field change of 90 kVcm-1 with only minor degradation of the functional properties (less than 5% of the maximum adiabatic temperature change). Hence, PMN-10PT can be considered as a promising material for use in an electrocaloric cooling device, but some critical issues that caused premature failure of several samples would need to be further addressed and improved.Vir: Journal of applied physics. - ISSN 0021-8979 (Vol. 128, iss. 10, Sep. 2020, str. 1-9)Vrsta gradiva - članek, sestavni delLeto - 2020Jezik - angleškiCOBISS.SI-ID - 31087619
Avtor
Del Duca, Manuel Gesù |
Tušek, Jaka |
Maiorino, Angelo |
Fulanović, Lovro |
Bradeško, Andraž |
Plaznik, Uroš |
Malič, Barbara |
Aprea, Ciro |
Kitanovski, Andrej
Teme
electrocaloric effect |
fatigue behavior |
ferroelectric ceramic |
elektrokalorični učinek |
doba trajanja |
feroelektrična keramika
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Del Duca, Manuel Gesù | |
Tušek, Jaka | 29624 |
Maiorino, Angelo | |
Fulanović, Lovro | 37469 |
Bradeško, Andraž | 36748 |
Plaznik, Uroš | 35399 |
Malič, Barbara | 04587 |
Aprea, Ciro | |
Kitanovski, Andrej | 18580 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: