Dielectric characterisation of ceramics from the ▫$TiO_2-TeO_2$▫ systemUdovič, Marko ; Valant, Matjaž ; Suvorov, DaniloCompositions from TiO2-TeO2 tie line were characterised using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and dilatometry. Results show ... that the only binary compound existing on the tie line is TiTe3O8. Single-phase TiTe3O8 was synthesised at 700°C in air and sintered at 720°C to ~95% of theoretical density. Such ceramics exhibit a relative permittivity of 50, a Qxf-value of 30,600 GHz and a temperature coefficient of resonant frequency (f) of +133 ppm/°C, measured at ~5 GHz. The concentration of structural defects in the TiTe3O8 grains is negligible which makes the dielectric properties of TiTe3O8 ceramics insensitive to variations in the heat-treatment conditions. The TiTe3O8 compound is chemically compatible with TeO2, which displays a negative temperature coefficient of resonant frequency (a relative permittivity of 19.3, a Qxf-value of 30,000 GHz and a temperature coefficient of resonant frequency of -119 ppm/°C for TeO2 ceramics with ~ 20% porosity) and can be used for compensation of the temperature coefficient of resonant frequency of the TiTe3O8 compound. Ceramics from the TiTe3O8-TeO2 subsystem can be sintered to >97% of theoretical density at temperatures as low as 670°C, which together with the fact that the ceramics exhibit a highly tunable f, relative permittivity around 30 and a Qxf-value of ~22,000 GHz suggests a potential for use in LTCC technology.Vir: Journal of the European ceramic society. - ISSN 0955-2219 (Vol. 21, 2001, str. 1735-1738)Vrsta gradiva - članek, sestavni delLeto - 2001Jezik - angleškiCOBISS.SI-ID - 16219687
Avtor
Udovič, Marko |
Valant, Matjaž |
Suvorov, Danilo
Teme
dielectric properties |
LTCC |
TiO2
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Udovič, Marko | 19821 |
Valant, Matjaž | 11991 |
Suvorov, Danilo | 08012 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: