Conversion of the Ms70 alpha-brass torsion-test data into hot-forming processing maps = Pretvorba podatkov torzijskega preizkusa alfa medi Ms70 v procesne zemljevide vroče predelave
Kubina, Tomáš ; Bořuta, Josef ; Pernis, Rudolf
The present paper gives a summary of the plastic behaviour of the Ms70 deep-drawing cartridge brass under the hot-forming conditions explored by using a SETARAM-Vítkovice torsion plastometer. The ...specimens were cut from the hot-extruded and, subsequently, cold-drawn brass bars. Formability tests were performed on the diameter 6 mm specimens at (650, 700, 750, 800 and 850) °C and at the speeds of (16, 80, 400 and 800) r/min. These testing conditions are equivalent to the conditions of the ordinary industrial hot extrusion of brass: the single most problematic operation in the manufacturing process in terms of an occurrence of serious defects. The results of the torsion tests were converted into the conventional format: the maximum flow-stress levels vs. the peak-strain intensity. The points thus obtained can be used for finding the activation energy for forming Q, which is useful for determining the thermally compensated strain rate with the aid of the Zener-Hollomon Z parameter. The power-dissipation maps with the axes showing the deformation temperature and logarithmic strain rate were computed using a dynamic material model. The calculation of the dissipation efficiency was verified by comparing it with the known data on the 30 % zinc brass. The maps constructed in this manner allow the data from the torsion and compression plastometers tobe compared. The paper also includes a discussion of the changes in the processing maps at higher strains showing the optimum regions for the hot extrusion of brass.
Bibliografsko gradivo je bilo uspešno dodano na polico.
Dodajanje bibliografskega gradiva na polico ni uspelo.
Gradivo je že na polici.
Trajna povezava
URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto
Faktor vpliva
Izdaja
Kategorija
Razvrstitev
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Izberite knjižnično izkaznico:
Baze podatkov,
v katerih je revija indeksirana
Ime baze podatkov
Področje
Leto
Povezave do osebnih bibliografij avtorjev
Povezave do podatkov o raziskovalcih v sistemu SICRIS
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Citiranje
Funkcionalnost trenutno ni na voljo. Prosimo, poskusite kasneje.
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi