Cu
O nanomaterials with well-defined facets and uniform size were synthesized by a wet-chemical method. Regardless of the additive composition, powders crystallize mostly in cuprite form. To compare ...their electrochemical behavior, the obtained materials were deposited on carbon glassy electrodes. The response to glucose from the materials with different exposed facets was recorded with a delay at the anodic curve. The chronoamperometric analyses (AMP) exhibited a lower signal in contrast to the cyclic voltammetry data (CV), indicating that the number of active sites involved in glucose oxidation processes resulting from the structure of the material is insufficient. For samples with dominant (100) or (111) planes, a typical characteristic was observed, however, with an additional peak at the anodic curve. The location of the peaks is approximately the same and no significant differences from the AMP and CV analysis were observed. The sample enclosed by the (111) facets exhibited higher activity; however, as a result of the redox reaction with glucose molecules, the surface state is changing. Cu
O materials enclosed by (100) planes exhibited optimal sensitivity as well as a large detective range. Samples with differential facet exposition present various current-potential profiles, as the effect of binder-particle interaction with Nafion.
Semiconductor photocatalysis is considered one of the most promising technologies for water purification from toxic organic dyes. However, to reliably evaluate the possibility of using a given ...material as a photocatalyst, it is crucial to investigate not only the photocatalytic activity but also its affinity towards various dyes and reusability. In this work, we studied the adsorptive/photocatalytic properties of hollow-spherical raspberry-like SnO2 and its SnO2/SnS2 heterostructures that were obtained via a chemical conversion method using three different concentrations of a sulfide precursor (thioacetamide). The adsorptive/photocatalytic properties of the samples towards cationic rhodamine B (RhB) and anionic indigo carmine (IC) were analyzed using uncommon wall zeta potential measurements, hydrodynamic diameter studies, and adsorption/photodecomposition tests. Moreover, after conducting cyclic experiments, we investigated the (micro)structural changes of the reused photocatalysts by scanning electron microscopy and Fourier-transform infrared spectroscopy. The obtained results revealed that the sensitization of SnO2 resulted not only in the significantly enhanced photocatalytic performance of the heterostructures, but also completely changed their affinity towards dyes. Furthermore, despite the seemingly best photocatalytic performance, the sample with the highest SnS2 content was unstable due to its (micro)structure. This work demonstrates that dye adsorption/desorption processes may overlap the results of cyclic photodecomposition kinetics.
The era of ever-growing worldwide energy requirements demands the development of new methods of energy conversion, where the design of novel materials and the improvement of the efficiency of ...existing ones are of great importance ....
2D TiO2 thin films and 3D flower-like TiO2-based nanostructures, also decorated with SnO2, were prepared by chemical and thermal oxidation of Ti substrates, respectively. The crystal structure, ...morphology and gas sensing properties of the TiO2-based sensing materials were investigated. 2D TiO2 thin films crystallized mainly in the form of rutile, while the flower-like 3D nanostructures as anatase. The sensor based on the 2D TiO2 showed the best performance for H2 detection, while the flower-like 3D nanostructures exhibited enhanced selectivity to CO(CH3)2 after sensitization by SnO2 nanoparticles. The sensor response time was of the order of several seconds. Their fast response, high sensitivity to selected gas species, improved selectivity and stability suggest that the SnO2-decorated flower-like 3D nanostructures are a promising material for application as an acetone sensor.
The constant progress in novel nanomaterials synthesis has contributed to the rapid development of nonenzymatic glucose sensors. For working electrodes preparation, drop casting proved to be the most ...convenient and thus most widely applied method. However, appropriate interpretation of obtained electrochemical signal requires in-depth knowledge of limitations related to this technique. In this study, we prepared solutions based on commonly reported polymers for nanostructures immobilization and investigated their influence on copper sulfides distribution on the electrode. Characterization of suspensions properties and behavior of particles during droplet drying revealed that nonionic polyvinylpyrrolidone (PVP) was favorable for electrodes modification with copper sulfides in comparison with Nafion and chitosan. It ensured homogeneity of the suspension as well as the uniform coverage of the electrode surface with particles, what resulted in increased active surface area and, therefore, higher signal from glucose addition. On the other hand, when cationic chitosan was used as a binder, suspensions were agglomerated and, within dry deposits, a coffee-ring effect was observed. Appropriate adjustment of material and polymer interactions led to enhanced electrode electrochemical performance.
This work aims to demonstrate that the Fe
O
nanocrystals' adsorptive and photocatalytic properties can be adjusted by exposing the crystal facets that are functionalized. To this end, cube- and ...disc-like structures were synthesized using a metal ion-mediated hydrothermal route. Thereafter, some of the samples were annealed at 500 °C for 3 h. Our paper combines the experimental part with theoretical calculations of the obtained materials' band edge positions. The results reveal that-aside from hematite-the as-synthesized discs also contain γ-FeOOH and β-Fe
O
phases, which transform into α-Fe
O
during annealing. The hydrodynamic diameter, zeta potential, and adsorption kinetics measurements show that the cube-like samples exhibit the highest affinity for cationic, whereas the discs have an affinity for anionic dye. Measurements of the wall zeta potential also reveal that annealing the discs modifies their surface state and ability to adsorb molecules. Photocatalytic tests show that the as-synthesized powders have better photocatalytic performance toward methylene blue decomposition than the annealed ones. The observed small changes in the concentration of the MO during illumination result from the energy band structure of the cube-like crystal orientation.
The diversity of materials proposed for non-enzymatic glucose detection and the lack of standardized protocols for assessing sensor performance have caused considerable confusion in the field. ...Therefore, methods for pre-evaluation of working electrodes, which will enable their conscious design, are currently intensively sought. Our approach involved comprehensive morphologic and structural characterization of copper sulfides as well as drop-casted suspensions based on three different polymers—cationic chitosan, anionic Nafion, and nonionic polyvinylpyrrolidone (PVP). For this purpose, scanning electron microscopy (SEM), X-ray diffraction (XRD), and Raman spectroscopy were applied. Subsequently, comparative studies of electrochemical properties of bare glassy carbon electrode (GCE), polymer- and copper sulfides/polymer-modified GCEs were performed using electrochemical impedance spectroscopy (EIS) and voltammetry. The results from EIS provided an explanation for the enhanced analytical performance of Cu-PVP/GCE over chitosan- and Nafion-based electrodes. Moreover, it was found that the pH of the electrolyte significantly affects the electrocatalytic behavior of copper sulfides, indicating the importance of OHads in the detection mechanism. Additionally, diffusion was denoted as a limiting step in the irreversible electrooxidation process that occurs in the proposed system.
The aim of the work was to obtain copper (I) selenide Cu2Se material with excellent thermoelectric properties, synthesized using the hydrothermal method and densified by the spark plasma sintering ...(SPS) method. Chemical and phase composition studies were carried out by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) methods. Measurements of thermoelectric transport properties, i.e., electrical conductivity, the Seebeck coefficient, and thermal conductivity in the temperature range from 300 to 965 K were carried out. Based on these results, the temperature dependence of the thermoelectric figure of merit ZT as a function of temperature was determined. The obtained, very high ZT parameter (ZT~1.75, T = 965 K) is one of the highest obtained so far for undoped Cu2Se.
A relatively new approach to the design of photocatalytic and gas sensing materials is to use the shape-controlled nanocrystals with well-defined facets exposed to light or gas molecules. An abrupt ...increase in a number of papers on the synthesis and characterization of metal oxide semiconductors such as a TiO2, α-Fe2O3, Cu2O of low-dimensionality, applied to surface-controlled photocatalysis and gas sensing, has been recently observed. The aim of this paper is to review the work performed in this field of research. Here, the focus is on the mechanism and processes that affect the growth of nanocrystals, their morphological, electrical, and optical properties and finally their photocatalytic as well as gas sensing performance.
Flower-like TiO2 nanostructures were obtained by chemical oxidation of Ti foil using H2O2 combined with subsequent annealing. This paper offers an analysis of the phase transformation of 3D ...flower-like titanium dioxide nanostructures. The role of the annealing atmosphere, sample thickness, grain shape, and nanoflower size are discussed. The nanostructures were examined using SEM, XRD, and Raman spectroscopy. Due to the nature of these two processes, the morphology of these nanomaterials is complex, and is obtained through a reaction involving Ti foil and H2O2 at 80°C. A distinction is made between the layer composed of small grains at the substrate/oxide interface, elongated crystal-like structures, and outer spongle-like film. The annealing parameters, such as atmosphere (air or argon) and temperature (450 or 600 °C), affect phase composition. The photoelectrochemical performance of the anode based on flower-like TiO2 has been shown. The thickness and phase composition of the anodes are factors that strongly affect the photocurrent. The multiphase heterojunctions proposed for 3D flower-like TiO2 photoanodes in photoelectrochemical (PEC) cells suppose that the conduction band of anatase should be above rutile. The highest photoelectrochemical performance was obtained for a photoanode composed of 20–40% anatase and an associated thickness of 0.75–1.5 µm.